【摘 要】
：
Ni2P/SiO2 and bimetallic NiMP/SiO2 (M =Co,Fe,Mo,W;Ni/M atomic ratio=5) catalysts were prepared by the temperature-programmed reduction method.The catalysts and their precursors were characterized by means of UV-Vis DRS,H2-TPR,XRD,TEM,CO chemisorption and
【机 构】
：
Tianjin Key Laboratory of Applied Catalysis Science and Technology, Department of Catalysis Science
论文部分内容阅读
Ni2P/SiO2 and bimetallic NiMP/SiO2 (M =Co,Fe,Mo,W;Ni/M atomic ratio=5) catalysts were prepared by the temperature-programmed reduction method.The catalysts and their precursors were characterized by means of UV-Vis DRS,H2-TPR,XRD,TEM,CO chemisorption and NH3-TPD.Their performance for the deoxygenation of methyl laurate was tested on a fixed-bed reactor.The results show that the main phase was Ni2P in all catalysts,and M (M=Co,Fe,Mo,W) entered the lattice of Ni2P forming solid solution.Different from Fe and Co,the introduction of Mo and W into Ni2P/SiO2 reduced the phosphide particle size and increased the acid amount.In the deoxygenation reaction,the turnover frequency of methyl laurate increased on the catalysts in the order of NiMoP/SiO2,Ni2P/SiO2,NiWP/SiO2,NiFeP/SiO2 and NiCoP/SiO2,which is influenced by the size of phosphide particles and the interaction between Ni and M (M =Fe,Co,Mo or W).The introduction of the second metal (especially Mo and W) into Ni2P/SiO2 promoted the hydrodeoxygenation pathway.This is mainly attributed to the interaction between Ni and the second metal.Finally,the NiMoP/SiO2 catalyst was tested at 340 ℃,3 MPa,methyl laurate WHSV of 14 h-1 and H2/methyl laurate molar ratio of 25 for 132 h,and its deactivation took place.We found that the catalyst deactivation mainly resulted from carbonaceous deposit rather than the sintering of metal phosphide crystallites.
其他文献
Lithium-sulfur (Li-S) batteries are great candidates for energy storage systems,but need to overcome the issues of low sulfur utilization and polysulfide shuttling for use in large-scale commercial applications.Recently,quaternized polymers have received
The transition of the current energy infrastructure from fossil fuels to renewable energy sources is critical to the continuous prosperity of our society and economy.In order to accelerate the extensive adoption of the sustainable energy sources,challenge
The influence of tris(trimethylsilyl) borate (TMSB) as an electrolyte additive on lithium ion cells have been studied using Li/LiCo1/3Ni1/3Mn1/3O2 cells at a higher voltage,4.7V versus Li/Li+.1 wt％ TMSB can dramatically reduce the capacity fading that occ
A series of biopolymer based complex were manufactured by coordinating iron ions to the abundant amino-and sulfur-containing groups in the modified wool and used as heterogeneous Fenton-like photocatalyst for 4-chlorophenol (4-CP) degradation in the prese
The new V-MCM-41 molecular sieves with good ordered hexagonal mesoporous structure and crystallinity were synthesized through in-situ hydrothermal preparation method.The effects of the crystallization time were discussed.The synthesized samples were chara
The potential application of electrochemically formed copper sulfide as horseradish peroxidase mediator in the enzymatic biofuel cell and anthraquinone AV109 dye as a fuel is investigated.The open circuit voltage of 0.52 V and short circuit current of ～3.
PtRu/SnO2/C catalyst was prepared in a polyol process,followed by reduction treatment and alkaline etching.X-ray diffraction,transmission electron microscope with energy dispersive spectrometer and Xray photoelectron spectroscopy were used to characterize
Direct ethanol fuel cells have attracted attention as an alternative energy technology due to several advantages such as high theoretical energy density and abundant supply of ethanol.In spite of the advantages,commercialization of direct ethanol fuel cei
Current study reports a rapid one-pot non-hydrolytic condition in the synthesis of SnO2 QDs nanopowder using tin (Ⅱ) stearate (Sn(St)2) as environmentally-benign organometallic precursor,which is an unprecedentedly employed-compound in preceding SnO2 nano
In this study,Ni/Y2Zr2O7 catalysts prepared with impregnation method and treated by dielectric barrier discharge plasma (DBD) in different atmospheres have been investigated for methane dry reforming.It is revealed by H2-TPR that plasma treatment can enha