La2O3 and Ce2O3 were penetrated into PbTiO3 to obtain conductive powders, and then they were mixed with polyurethane and butyl acetate to prepare conductive coatings. The results showed that the electric property of modified PbTiO3 powders was improved by penetration of La2O3 and Ce2O3. XRD patterns showed that some new compounds such as La2Ti6O15, CeTi21O38 and Pb0.634La0.209Ti0.948O2.284 were formed, which led to the rapid increase of conductivity. The resistivity of modified PbTiO3 powders decreased to 3.88 Ω·m. The coatings using modified PbTiO3 powders as fillings also had a good conductivity. When the PbTiO3 powders were 10% and antisettle agent (bentonite) content was 0.50%, and mass ratio between polyurethane and butyl acetate was 1.05, the surface resistivity of the coatings fell down to 1.3×108 Ω·m. This kind of conductive coatings could be used in electromagnetic shielding.
La2O3 and Ce2O3 were penetrated into PbTiO3 to obtain conductive powders, and then they were mixed with polyurethane and butyl acetate to prepare conductive coatings. The results showed that the electric property of modified PbTiO3 powders was improved by penetration of La2O3 and Ce2O3. XRD patterns showed that some new compounds such as La2Ti6O15, CeTi21O38 and Pb0.634La0.209Ti0.948O2.284 were formed, which led to the rapid increase of conductivity. The resistivity of modified PbTiO3 powders decreased to 3.88 Ω · m. The coatings using modified PbTiO3 powders When the PbTiO 3 powders were 10% and antisettle agent (bentonite) content was 0.50%, and the mass ratio between polyurethane and butyl acetate was 1.05, the surface resistivity of the coatings fell down to 1.3 × 108 Ω · M. This kind of conductive coatings could be used in electromagnetic shielding.