【摘 要】
：
Microstructure consisting of ferrite, bainite and retained austenite can be obtained through intercritical annealing and isothermal treatment in bainite transfo
【机 构】
：
College of Materials and Metallurgy,State Key Laboratory of Rolling and Automation
论文部分内容阅读
Microstructure consisting of ferrite, bainite and retained austenite can be obtained through intercritical annealing and isothermal treatment in bainite transformation region for low silicon TRIP (transformation induced plasticity) steel containing niobium. Effects of strain rate, Nb content and soaking temperature in bainite region on microstructure and mechanical properties of test steels were investigated. It is shown that as strain rate ranges from 10-2 to 10-4 s-1, the volume fraction of transformed martensite from retained austenite,as well as tensile strength, elongation rate and strength-ductility product, increases. When Nb is added, the volume fraction of retained austenite decreases, but tensile strength and yield strength increase. While Nb content reaches 0.014%, the steel exhibits high elongation and combination of strength and ductility. Higher retained austenite volume fraction and good mechanical properties are obtained in the test steels when the soaking temperature in bainite region is 400℃. The maximum values of tensile strength, total elongation rate and strength-ductility product can reach 739 MPa, 38% and 28082 MPa%, respectively.
其他文献
The glass forming ability of Gd-Co-Al ternary alloy systems with a composition ranging from 50% to 70% (molar fraction)for Gd and from 5% to 40% (molar fraction
Based on the available experimental information, the Ag-Si binary system was thermodynamically assessed using the CALPHAD method. The solution phases, including
Effect of activated carbon and electrolyte on electrochemical properties of organic supercapacitor was investigated. The results show that specific surface area
The crystal plasticity was implemented in the finite element method(FEM) software ABAQUS through the user subroutine UMAT. By means of discretizing the space at
The as-formed and post-deformed microstructures in both electroformed and spin-formed copper liners of shaped charge were studied by optical microscopy(OM), ele
This study investigated the rheological properties of semi-solid metal. An analytical model of apparent viscosity was built up based on analysis of energy dissi
Two Ti2Ni3Si/NiTi Laves phase alloys with chemical compositions of Ni-39Ti-11 Si and Ni-42Ti-8Si (%, mole fraction, the same below), respectively, were fabricat
La2/3Sr1/3Mn1-xZnxO3 films (x=0.05, 0.1, 0.3, and 0.5) were prepared using magnetron sputtering method, and the effect of Zn doping on transport properties of t
Ti-23Nb-0.7Ta-2Zr-O (TNTZO, molar fraction, %) alloy is a newly developed multifunctional β-type titanium alloy. This alloy was reported to deform via a unique
The enhancement of chemical absorption of CO2 by K2CO3/H2O absorbents in the presence of activated carbon (AC) particles was investigated. The results show that