A kind of Cu base composite reinforced by 0 1μm Al 2O 3 particles were prepared by hot pressing and sintering process for steel continuous casting mould. The microstructure and properties were studied. The results show that the Al 2O 3 particle distribution is uniform, and the particles refine the grain size. The tensile fracture is a mixture of quasi cleavage and dimple due to the moderate interface strength. As a result, the composite has better soft resistance and wear resistance than those of Cu and Cu alloy. With increase in super fine Al 2O 3, the density and electric conductivity of the composite decrease, but hardness and strength increase.
A kind of Cu base composite reinforced by 0 1 μm Al 2 O 3 particles were prepared by hot pressing and sintering process for steel continuous casting mold. The results show that the Al 2 O 3 particle distribution is uniform, and the particles refine the grain size. The tensile fracture is a mixture of quasi cleavage and dimple due to the moderate interface strength. As a result, the composite has better soft resistance and wear resistance than those of Cu and Cu alloys. With increase in super fine Al 2O 3, the density and electric conductivity of the composite decrease, but hardness and strength increase.