The manufacture process of 8mol% Y2O3 stabilized ZrO2(YSZ) from nano powders, including the forming and sintering stages, was studied. During the forming proces
论文部分内容阅读
The manufacture process of 8mol% Y2O3 stabilized ZrO2(YSZ) from nano powders, including the forming and sintering stages, was studied. During the forming process of YSZ powders, the relative density of YSZ increases lineally with the forming press,and the sintering linear shrinkage of YSZ to the forming press compiles to the parabola trend. When the forming press exceeding 500MPa, the samples with lower shrinkage and high density were obtained. The sintering temperature of YSZ decreases greatly because of the small size and high active surface of YSZ powders. As a result, the beginning sintering temperature of YSZ made in the experiment is as low as 825℃, and the end sintering temperature is 1300-1350℃. The relative density of YSZ ceramic by solid sintering at 1300-1350℃ is more than 97%, with little and small pores in the uniform microstructure.
其他文献
The heap leaching of oxide copper ores with copper cathode recovery by solvent extraction and electrowinning is now well established as a low-cost method of cop
Corrosion behaviors of pure Ni and three NiCr alloys were investigated in an HCl-containing oxidizing atmosphere at 700 ℃ and 800 ℃. All materials suffer from
Through morphology observation on silicon particles of Al-Si-Cu-Mg cast alloy, it is found that during solution treatment the evolution of eutectic silicon morp
The effect of extrusion on grain refinement has been studied in the AZ91 cast ingots. It is found that grain size smaller than 10 μm can be obtained by the ext
The stability of aqueous nano alumina powder suspensions with and without dispersant tri-ammonium citrate (TAC) was investigated by measuring zeta potential at
The new dust removal technical route using the carbon-granular bed filter,packed of carbon particles with appropriate grade derive from an online-process vibrat
Stirred tanks are used extensively in process industry and one of the most commonly used impellers in stirred tanks is the Rushton disk turbine.Surprisingly few
The compressive, shear strengths and abrasion-erosion resistance as well as flexural properties of two polypropylene fiber reinforced concretes and the comparis
Two-dimensional rigid-plastic finite element method (FEM) was used for simulation of the effect of process parameters on the static recrystallization of 60SiMnA
By using sub-overquenching and annealing method which has a wide processing window, (Nd, Pr)x(FeCoZr)94-xB6 (x=12, 10.5, 10, 9) bonded magnets were prepared and