【摘 要】
：
高精度小孔的加工目前国内尚未见用开齿质合金铰刀铰孔;尤其是1cr18Ni9Ti 不锈钢材料(工件图见图1),其孔深与直径之比为12/1.5=8,是属于较深小孔,且精度超过一级,而光洁度又
论文部分内容阅读
高精度小孔的加工目前国内尚未见用开齿质合金铰刀铰孔;尤其是1cr18Ni9Ti 不锈钢材料(工件图见图1),其孔深与直径之比为12/1.5=8,是属于较深小孔,且精度超过一级,而光洁度又要求▽9级,不圆度及锥度跳动偏差小于0.002,对这样高的精度、高光洁度的小孔加工是有不少困难的。改进前的加工方法系采用钻孔(φ1.3)—锪孔(φ1.45)—铰孔
At present, the machining of high-precision small holes has not been seen in the domestic use of reaming alloy reamers reaming; in particular, 1cr18Ni9Ti stainless steel (workpiece Figure 1), the hole depth and diameter ratio of 12 / 1.5 = 8, are more Deep holes, and the accuracy of more than one level, and the smoothness and requirements ▽ 9, non-circularity and taper runout deviation of less than 0.002, for such a high precision, high-precision hole processing is a lot of difficulties. Before the improvement of the processing method is the use of drilling (φ1.3) - countersink (φ1.45) - Reaming
其他文献
N,N-二壬氨基乙酸(DNG)在盐酸介质中萃取铑(Ⅲ)的低价配阴离子。运用最小电荷密度原理和氢键作用解释了铑(Ⅲ)配阴离子的萃取顺序。通过考察萃取平衡、萃取动力学和萃合物的
本文测量了置换反映:RE~(3+)+MgY~(2-)=REY~-+Mg~(2+)和RE~(3+)+MgZ~(3-)=REZ~(2-)+Mg~(2+)在离子强度I=0.10MNaClO_4,298.15K时的焓变(RE=La、Ce、Pr、Nd、Sm、Eu、Gd、Dy、
我队今年,一般是在5～10級岩石鑽进,其中有局部和个别的鑽孔,地层受断层影响,岩石过于破碎,以致个別鑽孔矿心采取率达不到地質要求,需要补量,造成反工。采用双重双动的合金質
前言近几年来,关于稀土镁中间合金化学分析的资料报导较多,我们对其分析方法也曾做过一些试验,由于攀枝花地区钒钛稀土球墨铸铁的日益推广,稀土镁中间合金的应用逐渐增多,为
在没有或不用齿厚游标卡尺直接测量齿条齿厚的情况下,用圆棒测量测出M值后,与标准M值比较,在多大的公差范围内,齿厚也在规定公差范围内。对这个实际生产中遇到的问题,我们进
在双波长分光光度计上连续浏定钛(Ⅳ)、铁(Ⅲ)已有报导。本文以一般的分光光度计根据“系数倍率法”原理,通过PC-1500计算机在钛(Ⅳ)及铁(Ⅲ)的DAPM络合物的吸收曲线上计算寻
目前,在沉积地球化学相和生油层的研究中,应用着为数甚多的指示标志。其中对沉积环境和成岩过程物理化学特征的主要因素——氧化—还原状况的研究,比较重视。在表明氧化—还
我厂生产精密磨床的砂轮架主轴,数量颇大,除少数采用氮化工艺外,大都采用9Mn2V工具钢或GCr15滚珠轴承钢,经锻造、球化、调质及机加工后,采用中频淬火机表面淬火的方法。由于
岩石硬度可由尖锐刃具开始钻进时的钻速表示,而研磨性可由钻速降低速度来确定。将磨锐的切削具钻进时的轴心压力作为硬度的量度单位,随着钻进时切削具的磨钝,为保持一定的给
欧洲球员一向以技术全面著称。从库科奇到诺维茨基,再到新近崛起的鲍里斯·迪奥,无一不是全能战士的代表,不过与库科奇和迪奥可以胜任多种位置不同的是,诺维茨基是把全能前锋