用ＤＳＣ研究了ＰＡ１０１０／６共聚物初生态及次生态样品的熔融行为，发现初生态样品的高温熔融峰（Ｔ１）和低温熔融峰（Ｔ２）对组成有不同的依赖关系；首次发现ＰＡ１０１０／６共聚物次生态的冷结晶现象，并讨论了冷结晶温度（ＴＣ）、冷结晶时间（ｔｃ）与组成的关系．
The melting behavior of primary and secondary samples of PA1010 / 6 copolymer was studied by DSC. It was found that the melting peak (T1) and the melting peak (T2) of the initial sample had different dependence on the composition. For the first time, PA1010 / 6 Copolymer cold secondary crystallization phenomenon, and to discuss the cold crystallization temperature (TC), cold crystallization time (tc) and the composition of the relationship.