Effect of different heat treatment process on damping peak of 6061Al/SiC_p MMC produced by spray co

• 作 者: 顾金海\\r\\r\\r\\r\\r\\r\\r\\r\\r\\n 张清霄\\r\\r\\r\\r\\r\\r\\r\\r\\r\\n 顾敏\\r\\r\\r\\r\\r\\r\\r\\r\\r\\n 王西科\\r\\r\\r\\r\\r\\r\\r
• 出 处: Transactions of Nonferrous Metals Society of China
• 发表日期: 2002年05期
• 关键词: spray damping

Effects of five typical heat treatment processes on the damping properties and the damping peak of 6061Al/SiC p MMC fabricated by spray codeposition were studied. The results show that the internal friction spectra of various heat treated samples exhibit the damping peak versus temperature between 130 ℃ and 200 ℃. Furthermore, the peak temperature as well as the peak height increases with increasing frequencies. By Arrhenius equation the active energy of the damping peak can be gotten, which is above 1 eV. On the other hand, different quenching treatments affect the damping peak remarkably, when the rate of cooling is above that of water quenching, the damping peak will shift to higher temperature as cooling speed is enhanced.

Effects of five typical heat treatment processes on the damping properties and the damping peak of 6061 Al / SiC p MMC fabricated by spray codeposition were studied. The results show that the internal friction spectra of various heat treated samples exhibit the damping peak versus temperature between 130 ° C By Arrhenius equation the active energy of the damping peak can be gotten, which is above 1 eV. On the other hand, different quenching regulations affect the the damping peak remarkably, when the rate of cooling is above that that water quenching, the damping peak will shift to higher temperature as cooling speed is enhanced.