【摘 要】
：
钒钛磁铁矿铁精矿含有大量TiO_2,由于炼铁后的铁渣成分复杂、TiO_2品位较低、杂质含量高,国内外至今都未利用。以钒钛铁精矿电炉熔化分离渣为原料进行了硫酸法回收TiO_2的试
【机 构】
：
冶金部有色金属研究总院三○一室六组
论文部分内容阅读
钒钛磁铁矿铁精矿含有大量TiO_2,由于炼铁后的铁渣成分复杂、TiO_2品位较低、杂质含量高,国内外至今都未利用。以钒钛铁精矿电炉熔化分离渣为原料进行了硫酸法回收TiO_2的试验。经过实验室和工业规模扩大试验,确定了最佳工艺条件,取得了较好的技术经济指标,得到了合格的焊条级钛白,生产成本比以钛铁矿为原料的硫酸法同类产品低。
Vanadium-titanium magnetite concentrate contains a large amount of TiO_2. Due to the complex iron-slag composition after iron-making, the TiO_2 has low grade and high impurity content, so far it has not been utilized at home and abroad. The recovery of TiO_2 by sulfuric acid method was carried out using vanadium - titanium - iron concentrate electric furnace melting slag as raw material. After laboratory and industrial expansion test to determine the best process conditions, and achieved good technical and economic indicators have been qualified electrode grade titanium dioxide, the production cost is lower than ilmenite-based sulfuric acid similar products.
其他文献
自六十年代以来,由于炼铁技术的飞跃发展,在高炉炼铁生产技术操作上,普遍采用精料、大风量、高风温、重负荷、大喷吹量的操作方针,进一步强化了冶炼,降低了焦比。但是,由于
波纹管具有减震、抗震、抗冲击和进行位移补偿的性能,故在航天、航空、石油、化工、冶金、机械、建筑、制冷等领域都得到了广泛的应用,特别是不锈钢波纹管兼有耐腐蚀、不易
目的对直肠癌患者血清中白细胞介素-2（IL－2）和可溶性白细胞介素-2受体（SIL－2R）进行检测。方法对IL－2和SIL－2R的检测均采用ELISA双抗夹心法。结果直肠癌患者手术前和手术后10~20d血清
心脏粘液瘤八例李庆新高秀峰吕国祯徐克劲董逸飞樊西林我院自１９８８年１月～１９９５年１２月共收治心脏粘液瘤患者８例，现报告如下。１临床资料与方法本组男６例，女２例。年龄１２～６５岁，平均２９岁。病程２～２４个月，平均６个月。肿
一、前言高炉炉底的侵蚀,大致有热侵蚀、化学侵蚀和机械磨损三种。在这三种侵蚀中,碳砖炉底以热侵蚀为主。碳砖炉底的设计亟需要考虑热侵蚀深度,以便设计最适宜的炉底厚
Fi
一九七八年十二月党的十一届三中全会上,党中央做出了把全党工作的着重点转移到社会主义现代化建设上来的英明决策。五中全会又在组织上进一步加强了党的领导,为实现四化建
一、环境中的稀散金属自然界中稀散金属分布广而量微,在地壳中各种稀散金属的丰度,除镓(15～19ppm)和锗(1.1～7ppm)稍高以外,其余均在1ppm左右或以下,如铊为0.6～1.3ppm,硒为0.05～0
一、前言随着现代化工农业的发展,要求钢的产品质量越来越高。为了满足这种要求,本世纪六、七十年代以来,世界各国在炼钢方面采用了很多措施。除了精料、铁水预处理、少渣或
我院１９８９～１９９６年共收治３５岁以下青年人胃恶性肿瘤３５例，其中误诊１３例，达３７％。现报告如下。作者单位：５１５０４１汕头大学医学院附一院外科（萧文成、白伟亮），病理科（黄杰雄）１临床资料１．１发病率同期共收治胃恶性肿瘤６２５例，３５岁以
总结了含钒钢渣返回烧结生产高钒烧结矿的半工业试验结果。含钒钢渣大配比返回烧结不仅是可行的,而且几项主要技术经济指标均有所改善。此次试验的特点是:含钒钢渣配比高(40%