导论臭氧侵蚀会使橡胶在垂直于外加应力的方向发生特征龟裂。这种降解是由臭氧与橡胶分子中的双键反应引起的。它导致断链并形成各种分解产物。许多作者对防止臭氧侵蚀橡胶的一般课题进行了综述。为了有效地控制橡胶的臭氧化,可以在不饱和橡
Introduction Ozone erosion causes rubber to crack in a characteristic perpendicular to the applied stress. This degradation is caused by the double bond reaction between ozone and the rubber molecules. It leads to chain scission and the formation of various decomposition products. Many authors have reviewed the general topics of preventing rubber from ozone attack. In order to effectively control the rubber ozonization, can be in unsaturated rubber