【摘 要】
：
Direct laser metal deposition is a kind of advanced rapid manufacturing technology,which can produce near net shape parts by depositing metal powders layer by layer.This study demonstrates fabrication,the anisotropy of mechanical properties and hardness o
【机 构】
：
School of Stomatology, China Medical University, Shenyang 110002, China;School of Materials Science
论文部分内容阅读
Direct laser metal deposition is a kind of advanced rapid manufacturing technology,which can produce near net shape parts by depositing metal powders layer by layer.This study demonstrates fabrication,the anisotropy of mechanical properties and hardness of a graded steel.The characteristics of constituent phases,microstructure,mechanical anisotropy,and microhardness were investigated using electron backscatter diffraction,optical microscopy,tensile test machine,and microhardness tester.It was found that the graded steel is dense and free of cracks.The crystal structures of the as-built samples evolved in three grades from fcc structures to fcc + bcc structures and then to bcc + fcc structures.Samples in x and z directions showed obvious mechanical anisotropy.The samples machined in x direction showed higher strength and lower elongation than those machined in z direction due to the presence of lack-of-fusion pores and the higher metallurgical bonding between layers in the x direction.The microhardness of the as-built samples increased along the cross section from the substrate (159.7 HV) to the top surface (545.4 HV).
其他文献
The corrosion behavior of high-strength steel used for flexible riser exposed to CO2-saturated saline solution and CO2-saturated vapor environments was studied through immersion experiment and electrochemical corrosion experiment.The corrosion behavior an
The effect of hot isostatic pressing (HIP) treatment on the fatigue notch sensitivity of Ti-6Al-4V alloy fabricated by electron beam melting (EBM) was investigated.The results indicate that the fatigue notch sensitivity of the as-fabricated samples is muc
Porous titanium scaffold with suitable porous architecture exhibits enormous potentials for bone defect repairs.However,insufficient osteointegration and osteoinduction still remain to open as one of the major problems to achieve satisfactory therapeutic
The study conveys an idea to enhance the osseointegration of titanium implant (Ti) through modulating macrophages M2 polarization.The ～ 100 nm spherical mesoporous silica nanoparticles (MSN) that compromised of ～ 4-nm-diameter nanotunnels were synthesized
The residual stress evolution in a safe-end/nozzle dissimilar metal welded joint of CAP1400 nuclear power plants was investigated in the manufacturing process by finite element simulation.A finite element model,including cladding,buttering,post-weld heat
The effects of Ni content and ball milling time on the hydrogen storage thermodynamics and kinetics performances of asmilled La5Mg95-xNix(x =5,10,15) ternary alloys have been investigated.The evolution of microstructure and phase of experimental alloys in
A large amount of directional and willow-like β\'phase was precipitated in Mg-10Gd-3Y-0.4Zr (GW103K) alloy after solution treatment and subsequently aged treatment (T6).In order to explore the effect of the precipitates on the corrosion behavior of the
Nanocrystalline and amorphous NdMg12-type NdMg11Ni +x wt％ Ni (x=100,200) alloys were successfully prepared through ball milling (BM).The microstructures and electrochemical properties were systematically studied to get a more comprehensive understanding o
The effect of phosphorus on the precipitations of γ“,γ\'and δ phases and associated tensile properties in IN718C alloy are investigated in this study.It is revealed that P atoms are dissolved in the grain interior to a relatively high degree and hence i
In order to study the influence of the physical state of solder on the interfacial reaction of dip-soldered Sn-3.0Ag-0.5Cu/Cu system,two kinds of experiments were designed,including:(1) solid-state aging between the solder and Cu substrate;(2) liquid-stat