The strain rate sensitivity to creep of single crystal Cu(110), metal tantalum, and 128oY-X LiNbO3 piezoelectric single crystal were measured at room temperature by MTS Nanoindenter XP. Among the three kinds of materials studied, Cu showed the highest degree of resistance to creep-induced deformation, which is followed by Ta, while the LiNbO3 single crystal deformed more readily than the others. The values of the steady-state strain rate sensitivities determined by the indentation methods are in the range of 0.002-0.006, 0.02-0.06 and 0.02-0.03 for Cu, Ta, and LiNbO3, respectively. The mechanisms for the indentation-induced creeping behavior and the factors that influenced the creeping are discussed.
The strain rate to creep of single crystal Cu (110), metal tantalum, and 128oY-X LiNbO3 piezoelectric single crystal were measured at room temperature by MTS Nanoindenter XP. Among the three kinds of materials studied, Cu showed the highest degree of resistance to creep-induced deformation, which is followed by Ta, while the LiNbO3 single crystal deformed more readily than the others. The values of the steady-state strain rate sensitivities determined by the indentation methods are in the range of 0.002-0.006, 0.02- 0.06 and 0.02-0.03 for Cu, Ta, and LiNbO3, respectively. The mechanisms for the indentation-induced creeping behavior and the factors that influenced the creeping are discussed.