The Cr-/Si-modified Ni Al Hf coatings were produced on single-crystal(SC) superalloy N5 by electron beam physical vapor deposition(EB-PVD). The cyclic oxidation behavior of the coatings at 1100 °C was investigated. The microstructures of the oxide scales grown on the coatings were characterized by scanning electron microscope(SEM) with energy-dispersive X-ray spectrum(EDX),electron probe micro-analyzer(EPMA) and X-ray diffraction(XRD). The effects of Cr and Si on the cyclic oxidation behavior of the Ni Al Hf coatings were discussed. The addition of Si to the Ni Al Hf Cr coating not only reduces the oxidation rate but also enhances the oxide scale adherence.Owing to the addition of Si in the coating, the segregation of Cr and Mo beneath the oxide scale is effectively avoided,which contributes to enhancing oxide scale adherence.
The Cr- / Si-modified Ni Al Hf coatings were produced on single-crystal (SC) superalloy N5 by electron beam physical vapor deposition (EB-PVD). The cyclic oxidation behavior of the coatings at 1100 ° C was investigated. of the oxide scales grown on the coatings were characterized by scanning electron microscope (SEM) with energy-dispersive X-ray spectrum (EDX), electron probe micro-analyzer (EPMA) and X-ray diffraction and Si on the cyclic oxidation behavior of the Ni Al Hf coatings were discussed. The addition of Si to the Ni Al Hf Cr coating not only reduces the oxidation rate but also enhances the oxide scale adherence. , the segregation of Cr and Mo beneath the oxide scale is effectively avoided, which contributes to enhancing oxide scale adherence.