The La-Mg-Ni system PuNi3-type La0.5Ce0.2Mg0.3Co0.4Ni2.6-xMnx (x=0, 0.1, 0.2, 0.3, 0.4) hydrogen storage alloys were prepared by casting and rapid quenching. Th
【机 构】
：
Department of Functional Material Research,School of Material,School of Materials Science and Engine
论文部分内容阅读
The La-Mg-Ni system PuNi3-type La0.5Ce0.2Mg0.3Co0.4Ni2.6-xMnx (x=0, 0.1, 0.2, 0.3, 0.4) hydrogen storage alloys were prepared by casting and rapid quenching. The effects of the rapid quenching on the structure and electrochemical characteristics of the alloys were studied. The results obtained by XRD, SEM and TEM indicate that the as-cast and quenched alloys mainly consist of two major phases, (La,Mg)Ni3 and LaNi5, as well as a residual phase LaNi. The rapid quenching does not exert an obvious influence on the phase composition of the alloys, but it leads to an increase of the LaNi5 phase and a decrease of the (La, Mg)Ni3 phase. The as-quenched alloys have a nano-crystalline structure, and the grain sizes of the alloys are in the range of 20-30 nm. The results by the electrochemical measurements indicate that both the discharge capacity and the high rate discharge(HRD) ability of the alloy first increase and then decrease with the variety of quenching rate and obtain the maximum values at the special quenching rate which is changeable with the variety of Mn content. The rapid quenching significantly improves the cycle stabilities of the alloys, but it slightly impairs the activation capabilities of the alloys.
其他文献
It iS known that the strength of alloys can be successfully improved by rapid solidification. The paper presents a process where Cu-Cr-Sn-Zn lead frame alloy is
Steady-state corrosion and wear behaviors of two Al-bronzes, Cu-14Al-X and QAl9-4, in 5.0% H2SO4 solution were investigated. It is found that wear loss of bronz
Multilayer ceramic sheets composed of Li1.075Nb0.625Ti0.45O3 (LNT) layers and silver metal layers were fabricated by aqueous tape-casting method. LNT green tape
Highly efficient phosphors under vacuum ultraviolet excitation are still demanded for the development of plasma display panels and Hg-free fluorescent lamps. Th
AZ31 Mg alloy bar was subjected to 8-pass equal-channel angular pressing(ECAP) at 623 K. Microstructure evolution was observed by optical microscopy(OM) on cros
Gray cast irons were inoculated with FeSi75+RE and FeSi75+Sr inoculants. The changes of apex angle of the drills before and af-ter being used were used to evalu
CuInSe2 (CIS) precursor films have been prepared by electrodeposition in aqueous solution. The electrodeposited films were characterized by X-ray diffraction (X
During thermal debinding in ceramic injection molding, the inhomogeneity of green body is a key origin of cracks. In this study, the impact of low molecular wei
目的 应用多b值DWI序列评估前列腺癌内分泌治疗后扩散与灌注信息的改变情况.方法 10例前列腺癌内分泌治疗后患者及12例前列腺癌患者被纳入研究.所有患者均经超声引导下前列腺
目的 评价3D T2WI在子宫内膜癌MR盆腔检查的图像质量及肿瘤检出和分期的应用价值.方法 前瞻性收集30例子宫内膜癌首诊病例,盆腔MR检查轴位、斜冠状位、矢状位T2扫描,时间共12