Magnetite(Fe_3O_4) nanoparticles with different sizes and shapes are synthesized by the thermal decomposition method.Two approaches,non-injection one-pot and hot-injection methods,are designed to investigate the growth mechanism in detail.It is found that the size and shape of nanoparticles are determined by adjusting the precursor concentration and duration time,which can be well explained by the mechanism based on the LaMer modei in our synthetic system.The monodisperse Fe_3O_4 nanoparticles have a mean diameter from 5nm to 16 nm,and shape evolution from spherical to triangular and cubic.The magnetic properties are size-dependent,and Fe_3O_4nanoparticles in small size about 5nm exhibit superparamagnetic properties at room temperature and maximum saturation magnetization approaches to 78 emu/g,whereas Fe_3O_4 nanoparticles develop ferromagnetic properties when the diameter increases to about 16 nm.
Magnetite (Fe_3O_4) nanoparticles with different sizes and shapes are synthesized by the thermal decomposition method. Two approaches, non-injection one-pot and hot-injection methods, are designed to investigate the growth mechanism in detail. It is found that the size and shape of nanoparticles are determined by adjusting the precursor concentration and duration time, which can be well explained by the mechanism based on the LaMer modei in our synthetic system. monodisperse Fe_3O_4 nanoparticles have a mean diameter from 5 nm to 16 nm, and shape evolution from spherical to triangular and cubic. magnetic properties are size-dependent, and Fe_3O_4nanoparticles in small size about 5nm exhibit superparamagnetic properties at room temperature and maximum saturation magnetization approaches to 78 emu / g, and Fe_3O_4 nanoparticles develop ferromagnetic properties when the diameter increases to about 16 nm.