摘 要：以Sb2O3为催化剂，通过熔融法来实现端羟基聚酯树脂的合成，其中，使用15%、35%、55%的有机硅中间体进行化学改性，以偏苯三甲酸酐对有机硅改性后的聚酯进行封端，并以二甲基乙醇胺成盐来制备水性有机硅改性聚酯树脂，配以氨基树脂进行固化后测评机械性能。研究表明，有机硅含量在30%左右，制得的水性有机硅改性聚酯树脂耐高温性良好、硬度较强、柔韧性符合标准，此时的改性聚酯树脂的性价比最具优势。
关键词：聚酯树脂;有机硅中间体;化学改性
Abstract：Hydroxy-terminated polyester resin was synthesized by using Sb2O3 as catalyst through melting method，in which modified with 15%、35%、55% intermediate of organosilicon. Then we terminated the modified polyester resin with TMA ，salified with DMEA，and obtained the waterborne organosilicon-modified polyester resin，which was evaluated mechanical properties by solidified with amino resin. Research indicated that waterborne organosilicon-modified polyester resin has better properties in thermostability，rigidity and flexibility containing about 30% intermediate of organosilicon，which is most dominant in cost performance.
Key words： polyester resin; intermediate of organosilicon; chemical modified
一、化學作用分析
在通常的情况下，聚酯树脂的涂料部分十分光亮并且丰满，除此之外，还对金属物质的附着力有着良好的效果，硬度与耐溶剂性能以及在面对高温的状态下漆膜力学强度等条件下仍能保持十分优良的性能优势，能够与多种树脂实现相容，柔韧性与拉伸性能十分显著。另一方面，有机硅树脂的优势体现在：在热氧化状态下能够保持稳定性能，电绝缘与不粘性方面的性能也十分优良，尤其是耐候性十分突出，尽管是处于紫外线较强的情况下也不会很容易出现泛黄的不良现象，但是，纯有机硅树脂也有一定的缺陷问题，其需要使用高温进行烘干，固化的时间十分漫长，在附着力以及耐溶剂方面的性能效果十分不理想，当温度比较高的情况下其漆膜的力学性能受到严重影响。当使用有机硅树脂来实现与饱和聚酯树脂的化学改性，则能够有效地发挥这两者之间的性能特征，两者之间能够形成两种性能较为突出的涂膜。笔者使用熔融法对端羟基聚酯树脂进行合成试验，通过道康宁有机硅的中间体实施改性工作，使用偏苯三甲酸酐展开水性化封端作业，利用N，N-二甲基乙醇胺成盐，合成了能够耐受高温、硬度较强、柔韧性性能完好的有机硅化学改性的水性饱以及聚酯树脂。
二、试验环节
1.试验仪器与药品成分介绍。本次试验将使用以下相关仪器与药品成分，内容如下：精密色差仪hp- 200、恒温水浴锅;恒温干燥箱、hz- d 型水循环式真空泵、实验室有机合成装置、tc830 涂层测厚仪、ndj- 1 旋转粘度计等相关试验仪器。化学工业品包括：99.5%对苯二甲酸（TPA）、（
关键词：聚酯树脂;有机硅中间体;化学改性
Abstract：Hydroxy-terminated polyester resin was synthesized by using Sb2O3 as catalyst through melting method，in which modified with 15%、35%、55% intermediate of organosilicon. Then we terminated the modified polyester resin with TMA ，salified with DMEA，and obtained the waterborne organosilicon-modified polyester resin，which was evaluated mechanical properties by solidified with amino resin. Research indicated that waterborne organosilicon-modified polyester resin has better properties in thermostability，rigidity and flexibility containing about 30% intermediate of organosilicon，which is most dominant in cost performance.
Key words： polyester resin; intermediate of organosilicon; chemical modified
一、化學作用分析
在通常的情况下，聚酯树脂的涂料部分十分光亮并且丰满，除此之外，还对金属物质的附着力有着良好的效果，硬度与耐溶剂性能以及在面对高温的状态下漆膜力学强度等条件下仍能保持十分优良的性能优势，能够与多种树脂实现相容，柔韧性与拉伸性能十分显著。另一方面，有机硅树脂的优势体现在：在热氧化状态下能够保持稳定性能，电绝缘与不粘性方面的性能也十分优良，尤其是耐候性十分突出，尽管是处于紫外线较强的情况下也不会很容易出现泛黄的不良现象，但是，纯有机硅树脂也有一定的缺陷问题，其需要使用高温进行烘干，固化的时间十分漫长，在附着力以及耐溶剂方面的性能效果十分不理想，当温度比较高的情况下其漆膜的力学性能受到严重影响。当使用有机硅树脂来实现与饱和聚酯树脂的化学改性，则能够有效地发挥这两者之间的性能特征，两者之间能够形成两种性能较为突出的涂膜。笔者使用熔融法对端羟基聚酯树脂进行合成试验，通过道康宁有机硅的中间体实施改性工作，使用偏苯三甲酸酐展开水性化封端作业，利用N，N-二甲基乙醇胺成盐，合成了能够耐受高温、硬度较强、柔韧性性能完好的有机硅化学改性的水性饱以及聚酯树脂。
二、试验环节
1.试验仪器与药品成分介绍。本次试验将使用以下相关仪器与药品成分，内容如下：精密色差仪hp- 200、恒温水浴锅;恒温干燥箱、hz- d 型水循环式真空泵、实验室有机合成装置、tc830 涂层测厚仪、ndj- 1 旋转粘度计等相关试验仪器。化学工业品包括：99.5%对苯二甲酸（TPA）、（