【摘 要】
：
为了寻求一种处理鋅废件的方法,曾在熔盐电解质內进行了粗鋅的电化学精炼試驗。电解质系采用分析純的氯化鋅与化学純的氯化鉀的混合物。这两种化合物的比例是1:1,熔点为270
论文部分内容阅读
为了寻求一种处理鋅废件的方法,曾在熔盐电解质內进行了粗鋅的电化学精炼試驗。电解质系采用分析純的氯化鋅与化学純的氯化鉀的混合物。这两种化合物的比例是1:1,熔点为270℃。电解精炼过程是在由两个坩堝組成的电解槽內进行的。外面的大坩堝作为阳极空間,其中装入粗金属,里面的小坩堝是阴极空間,純的鋅晶种即放入其中。使用鎢棒作导
In an effort to find a method of treating zinc scrap, an electrochemical refining test of crude zinc has been performed in molten salt electrolytes. Electrolytes are mixtures of analytical grade zinc chloride and chemically pure potassium chloride. The ratio of the two compounds is 1: 1 and the melting point is 270 ° C. The electrolytic refining process is carried out in an electrolytic cell consisting of two crucibles. Outside of the crucible as an anode space, which filled with coarse metal, which is a small crucible cathode space, pure zinc seed into which it is. Use tungsten rods as guides
其他文献
一、前言最近几年,在铸锭生产上采用了挂绝热板的上小下大钢锭模新工艺,这对提高钢锭收得率是一项有效的措施,在国内外己广泛采用。为了提高钢锭收得率和质量,消除二次缩孔,
本文对攀钢四一0厂0.8m～3试验高炉解剖后各部位焦炭显微构造的变化（例如块焦由表及里的气孔率变化,孔壁平均厚度及孔壁各显微构造含量的变化）进行了研究,并对焦炭孔壁各显微结构
业已成功地用各种生产方法从含镍红土矿中提取镍。较新的工艺包括诸如羟基肟,羧酸和螯合树脂的溶剂萃取法。在多段系统中,仅两段接触时间小于2分钟的提取过程就可达到100%回
十年来,电解銅的生产有飞跃的发展,不但在产量上逐年增加,1958年的实际产量为解放前最高年产量的数十倍;而且在增加产量的同时,由于采用职工群众合理化建議,推广先进经驗和
第二重型机器厂于7月22日首次生产了国内最大钢锭。钢锭重260吨,有24个棱角,径向最大尺寸为5054mm,总高6785mm。钢锭冒口铸出耳朵供脱模用,脱模时用150吨和200吨吊车各一台
笔者以Pb—Ni二元系及Pb—Ni—Fe三元系相图为依据,并利用PbO—FeO—NiO—Pb—Fe—Ni—O_2还原平衡体系結合原料組成进行計算,认为采用鉛富集偏析法处理低品位硅酸盐鎳矿,可
在锌的湿法生产中,使所积累的杂质(Na、K、Mg和Mn)维持在一定水平的唯一方法是从循环系统中排放出一卩分溶液。从排放出的这卩分溶液中回收锌和H_2SO_4,则可以通过各种不同
一、问题的提出自二次世界大战后,由于炼铁技术的发展,世界生铁产量逐年大幅度增加,焦煤益感不足,降低焦比已成为炼铁的关键问题之一。而降低焦比与提高风温、加大燃料(粉煤
近年来，对非霍奇金淋巴瘤（ＮＨＬ）的化疗随着化疗方案的更新，其有效率不断得以提高，我们自１９９４年５月—１９９７年１２月采用米托蒽醌（Ｍｉｔｏｘ－ａｎｔｒｏｎｅ，Ｎｏｖａｎｔｒｏｎｅ，Ｍｘ）、鬼臼乙叉甙（Ｅｔｏｐｏｓｉｄｅ，ＶＰ１６）为主的ＯＰＥＮ方...
In recent years, chemotherapy for non-Hod
本钢广大革命职工遵照毛主席关于“我们必须打破常规,尽量采用先进技术”的教导,在全国各兄弟单位的大力支援下,在五号高炉建设过程中采用了炉外燃烧室热风炉(简称外燃式热