【摘 要】
：
通过乳液聚合法合成无规苯丙乳液,然后与钛酸四丁酯混纺制备含Ti的复合纳米纤维,经高温煅烧成功制备了TiO_2纳米纤维。探讨了在乳液固含量与助纺剂PVA的质量比为8∶1时对在不
【机 构】
：
北京化工大学化工资源有效利用国家重点实验室,
论文部分内容阅读
通过乳液聚合法合成无规苯丙乳液,然后与钛酸四丁酯混纺制备含Ti的复合纳米纤维,经高温煅烧成功制备了TiO_2纳米纤维。探讨了在乳液固含量与助纺剂PVA的质量比为8∶1时对在不同的煅烧温度下所得纤维的形貌及TiO_2晶型的影响。采用扫描电镜(SEM)和X射线晶体衍射(XRD)对产物进行了表征。探究了制得的TiO_2纳米纤维在紫外光下对亚甲基蓝的光催化降解活性。
The random styrene-acrylic emulsion was synthesized by emulsion polymerization and then mixed with tetrabutyl titanate to prepare Ti-containing composite nanofibers. The TiO 2 nanofibers were successfully prepared by high-temperature calcination. The effect of the solid content of the emulsion and PVA at the mass ratio of 8: 1 on the morphologies of the obtained fibers and the crystalline forms of TiO 2 at different calcination temperatures was investigated. The products were characterized by scanning electron microscopy (SEM) and X-ray crystallography (XRD). The photocatalytic degradation activity of methylene blue on TiO 2 nanofibers was investigated.
其他文献
通过微波辐射技术,采用二步法合成纳米TiO_2/聚乳酸(PLA)复合材料,借助FT-IR、和SEM等技术对样品进行结构表征。结果表明,处理后的纳米TiO_2和PLA之间存在相互作用,能够均匀
采用水热法,以氧化石墨烯为模板,成功合成了NaErF_4六棱柱状微米棒。通过X射线衍射(XRD)、扫描电子显微镜(SEM)和透射电子显微镜(TEM)等对合成样品的物相结构及晶粒形态进行
传统的物理教学中很多老师都认为学生年龄太小,对知识的理解挖掘不用太深只需要掌握知识即可,却遗漏了学生的生活态度和价值观各方面的养成也会受到物理知识的影响,可是物理
以石蜡和经硝酸处理过的碳纳米管(CNTs)为原料,苯为溶剂,采用真空渗透法制备了纳米胶囊相变材料,并通过透射电镜、红外光谱、差示热量(DSC)等测试方法对样品进行了表征。结果
护生职业综合素质的养成,是一个渐进的过程.需要院校通识公共课程师及专业教师完成医学基础与专科教学同时,结合大学生岗位社会实践的要求,开展对接职业的专业性岗位实践,促
幼儿期是接受美术教育的最有利的年龄阶段,美术教育对于人的想象力和创造力的积极作用以及潜在的影响是其他教育所难以替代的.本文通过社区与幼儿园的互动,打破常规,形成资源
[摘 要] 随着教育体制改革的不断加深，對高校发展提出了更加严格的要求。为了适应时代发展，推动高校协同创新和人才培养，必须加强高校管理，创新管理模式。精细化思想在高校工会管理中产生了积极作用。对精细化思想在高校工会管理中的应用进行了研究，希望对高校工会管理向规范化发展提供一些借鉴。 [关 键 词] 高校工会；精细化思想；管理 [中图分类号] G647 [文献标志码] A [文章编号] 2096
在70℃的酸性水溶液中,以氧化石墨烯为氧化剂,实现了吡咯的原位氧化聚合。采用傅里叶红外光谱(FTIR),X射线衍射(XRD),X射线光电子能谱(XPS)、扫描电子显微镜(SEM)和透射电子
在当前的教学背景下,越来越多的教师意识到了教学改革的重要性,初中生物教师同样如此,许多教师发现传统的政治灌输式教育方法已经难以满足学生的成长和发展需求,所以必须对教
采用水热合成法制得二硫化钼(MoS2)粉末,详细研究了水热时间对产物形貌及光催化降解性能的影响.首先采用粉末X射线衍射仪(XRD)和场发射扫描电子显微镜(FE-SEM)对产物MoS2进行