A new niobate Ba3NaBiNb10O30 was synthesized by the solid state reaction.The reaction mixture was characterized by thermogravimetric and differential thermal an
论文部分内容阅读
A new niobate Ba3NaBiNb10O30 was synthesized by the solid state reaction.The reaction mixture was characterized by thermogravimetric and differential thermal analysis (TG-DTA),X-ray diffraction and dielectric constant measurements.The results show that Ba3NaBiNb10O30 has an orthorhombic tungsten bronze structure with space group Cmm2 and the unit cell parameters are a=1.7660(1) nm,a=1.7626(1) nm,c=0.78621(6) nm,Z=4.Ba3NaBiNb10O30 undergoes two phase transitions at 200℃ and 400℃,respectively.
其他文献
The effects of promoters K, Ba, Sm on the chemisorption and desorption of hydrogen and nitrogen,dispersion of metallic Ru and catalytic activity of active carbo
An experimental system was setup to study the pressure field of unconfined vapor cloud explosions.The semi-spherical vapor clouds were formed by slotted 0.02 mm
Split-root solution culture was used to study the promoting effect of lanthanum on rice (Oryza sativa) growth and its physiological mechanisms. Results show tha
A 3D unsteady state numerical model of heat transfer in the circumferential laser oxygen cutting of pipes wasdeveloped. In order to minimize the computing time
准等熵压缩实验技术已用来研究材料在高压下的状态方程.基于聚龙一号装置平台,实现对样品的准等熵压缩和超高速飞片发射,进行了一系列实验来加深对负载构型的理解.通过对负载
The microstructure and properties of tetrahedral amorphous carbon (ta-C) films deposited by the filtered cathodic vacuum arc technology has been investigated by
By using some elementary inequalities, authors in this paper makes further improvement for estimating the heights of Bézier curve and rational Bézier curve. A
Wiistite-based catalyst for ammonia synthesis exhibits extremely high activity and easy to reductionunder a wide range of conditions. The reaction kinetics of a
The transparent PVC films were prepared by tape casting. In the process of preparation, rare earth nitrate, as a kind of modifier, was added to the solution of
An experimental study of vertical gas conveying of Geldart-D powder as a dilute phase is performed ina pipe of length 22 m and internal diameter 0.05 m using a