【摘 要】
：
淬硬钢(HRC40～62)及铸铁(HB240kgf/mm~2)旋转体工件的精加工和半精加工,一般都用车削工艺,刀具用 T30K4,T15K6,BK6,BK8硬质合金车刀(刀片以焊接或机械固定),但是切削速度只能
论文部分内容阅读
淬硬钢(HRC40～62)及铸铁(HB240kgf/mm~2)旋转体工件的精加工和半精加工,一般都用车削工艺,刀具用 T30K4,T15K6,BK6,BK8硬质合金车刀(刀片以焊接或机械固定),但是切削速度只能为未淬火结构钢件切削速度的1/2～1/6.而且刀具寿命极短。为寻找新的耐磨刀具材料,苏联正式生产了陶瓷切削材料B3,BOK-60,BOK-63。同时对这些材料的切削性能也进行了广泛的研究。对陶瓷刀片 B3,BOK-60,BOK-63的磨损起着
The machining and semi-finishing of hardened steel (HRC40 ~ 62) and cast iron (HB240kgf / mm ~ 2) rotating body parts are generally used turning technology, T30K4, T15K6, BK6, BK8 Carbide turning tools To welding or mechanical fixed), but the cutting speed can only quench the structural steel cutting speed of 1/2 ~ 1 / 6. And the tool life is very short. To find new wear-resistant tool material, the Soviet Union formally produced the ceramic cutting material B3, BOK-60, BOK-63. At the same time, the cutting performance of these materials has also been extensively studied. Wear on ceramic inserts B3, BOK-60, BOK-63
其他文献
用MOCVD技术在偏(100)GaAs衬底上生长了发光波长在1·3μm的线状空间规则排列InAs量子点.光致发光实验表明,相对于正(100)衬底,偏(100)GaAs衬底上生长的InAs量子点具有更好的
印度科学院研制了一种铝和颗状石墨的复合铸件,它具有良好的耐磨性能,在负荷、速度适中,并有润滑的条件下(包括界面润滑),这些合金可以代替常用的铜、铅、锡基轴承合金。这
本文对沿着红河断裂带及其以北地区,滇西北——滇南约10万平方公里范围内,通过对24个地震台所记录的9次(M=3.4—5.5)地震震相分析研究所作的 P_n 波相遇时距曲线和地壳结构轮
在冬季为了加速水玻璃芯硬化速度,经过试验与生产证实,在芯砂中加入催硬剂硫酸亚铁后,硬化速度加快,成本降低,工效提高,并保证了铸件质量。一、硫酸亚铁作催化剂的机理硫酸
要发展市场经济,我们面临的一个突出的困难是市场发育问题。由于我国长期以来实行计划经济,因而市场机制不健全,市场不发育是众人皆知的缺陷。为此,必须加速培育市场,不断增
本文阐述了应用氯指示找矿的地球化学依据,并且通过对一些矿床实际资料的归纳总结,分析了某些金属矿床中氯的地球化学异常特征,最后指出了应用氯指示找矿的实际意义。
This
使用立钻对轴类零件沿轴向进行孔加工时,对工件的定位方法很多,现介绍我厂使用的一种用凸轮夹紧的自动定心夹具。这种夹具能对一定直径尺寸范围内的轴类零件进行轴向孔加工,
激光加工是用光作热源的热加工,主要用于钻孔、切割、焊接、热处理、划线、去重等等。图1所示为激光加工的示意图(关于“激光热处理”参阅本刊的1980年第五期)。
Laser pro
The dynamic response of moored crane-ship is studied. Governing equations for the dynamic response of a crane-ship coupled with the pendulum motion of the paylo
小秦岭地区是我国的重要黄金矿产基地之一。它位于秦岭纬向构造带北侧,在前震旦系强烈混合岩化的变质岩系中广泛分布着含金石英脉,矿化范围东西长约80—100公里,南北宽约10