Mixed mode Ⅰ/Ⅱ fracture erperiments of LC4-CS aluminum alloy were conductedby using tension--shear specimens with thicknesses of 2, 4, 8 and 14mm. Fracturemechanisms of thickness effect on mixed mode Ⅰ/Ⅱ fracture were first examined fromfracture surface morphology to correlate with the macroscopic fracture behavior andstress state. It is found that specimen thickness has a strong influence on mixed modefracture. As thickness varies from thin to thick the macroscopic fracture surfacesappear the characteristics of plane stress state (2mm, 4mm--thick specimen), three--dimensional stress state (8mm--thick specimens), and plane strain state (14mm--thickspecimens), respectively. The specimens of all kinds of thicknesses are typical of ten-sile type failure under mode Ⅰ loading condition and shear type failure under mode Ⅱloading condition. Two distinct features coexist on the fracture surfaces under mixedmode loading conditions, and the corresponding proportion varies with loading mix-ity. Void--growth
Mixed mode Ⅰ / Ⅱ fracture erperiments of LC4-CS aluminum alloy were conducted by using tension - shear specimens with thicknesses of 2, 4, 8 and 14mm. Fracture mechanisms of thickness effect on mixed mode Ⅰ / Ⅱ fracture were first examined from fractured surface morphology to correlate with the macroscopic fracture behavior andstress state. It is found that the thickness of a macroscopic fracture behavior andstress state. (2mm, 4mm - thick specimen) Three - dimensional stress state (8mm - thick specimens), and plane strain state (14mm - thickspecimens), respectively. The specimens of all kinds of thicknesses are typical of ten-sile type failure under mode Ⅰ loading condition and shear type failure under mode Ⅱloading condition. Two distinct features coexist on the fracture surfaces under mixed mode loading conditions, and the corresponding proportion varies with loadin g mix-ity. Void - growth