Magnesium stress corrosion cracking

• 作 者: N. Winzer A. Atrens W. Dietze
• 机 构: MaterialsEngineering,SwissFederalLaboratoriesforMaterialsScienceandTechnology,GKSS-Forschungszentrum
• 出 处: 中国有色金属学会会刊：英文版
• 发表日期: 2007年A01期
• 关键词: 压力 抗腐蚀强度 氢化合物 合金 stress corrosion cracking linearly increasing stress test LIS
• 基金项目: AcknowledgementsThis research was supported by an ARC Linkage Grant in collaboration with the GM Technical Centre at Warren Mi. N. Winzer and A. Atrens also wish to thank GKSS-Forschunszentrum GmbH fo

The significant positive green environment influence of magnesium alloy usage in transport could be compromised by catastrophic fast fracture caused by stress corrosion cracking(SCC). Transgranular stress corrosion cracking(TGSCC) of AZ91 was evaluated us