Anticorrosion properties of enamels with high B2O3—P2O5—AlPO4 content in molten aluminum

• 作 者: 周鸣 李克 孙宝德 疏达 王俊
• 机 构: SchoolofMaterialsScienceandEngineering
• 出 处: 中国有色金属学会会刊：英文版
• 发表日期: 2002年3期
• 关键词: B2O3-P2O5-AlPO4 涂漆 熔铸铝合金 电子探针 耐蚀性 enamel molten Al corrosion interface elect

The new enamels with high H3BO3-(NH4)2 HPO4-AlPO4 content were studied, and the melting temperature of the enamels was adjusted by adding carbonate of alkali metal and alkaline earth metal. The enamels could spread slightly in the molten Al alloy observed