Silicon was added to improve the tensile, wear and creep behaviors of AM60 magnesium alloy in this study. The investigation has been undertaken by means of universal testing machine, HBE-3000A Brinell hardness tester, M-2000 friction-wear machine, DMA-Q800 creep machine, optical microscopy (OM) and scanning electron microscopy (SEM). The results indicate that the Chinese script type Mg2Si particles are formed by adding Si into the AM60 magnesium alloy. The ultimate tensile strength and hardness of the AM60 magnesium alloy increases with the Si addition, and the ultimate tensile strength and hardness of the AM60+1.0wt.%Si alloy are increased by 12% and 19.8%, respectively in comparison with that of the AM60 magnesium alloy. The wear property and the high temperature creep property of the AM60 magnesium alloy are also improved with Si addition. The wear mechanisms of the AM60 and AM60+1.0wt.%Si alloys are adhesive wear and abrasion wear, respectively. While, the elongation of the AM60 magnesium alloy decreases with the addition of Si. The optimum Si addition content is 1.0wt.%.
Silicon was added to improve the tensile, wear and creep behaviors of AM60 magnesium alloy in this study. The investigation has been undertaken by means of universal testing machine, HBE-3000A Brinell hardness tester, M-2000 friction-wear machine, DMA-Q800 The results indicate that the Chinese script type Mg2Si particles are formed by adding Si into the AM60 magnesium alloy. The ultimate tensile strength and hardness of the AM60 magnesium alloy increases with hardness the Si addition, and the ultimate tensile strength and hardness of the AM60 + 1.0 wt.% Si alloy are increased by 12% and 19.8%, respectively in the comparison with the AM60 magnesium alloy. The wear property and the high temperature creep property of the AM60 magnesium alloy are also improved with Si addition. The wear mechanisms of the AM60 and AM60 + 1.0 wt.% Si alloys are adhesive wear and abrasion wear, respectively. While, the elongation of the AM60 ma gnesium alloy decreases with the addition of Si. The optimum Si addition content is 1.0 wt.%.