【摘 要】
：
以高锰酸钾为锰源,甘氨酸为模板在硝酸体系中仿生合成纳米二氧化锰。利用SEM、XRD、N2吸附脱附对制得样品进行表征,通过改变反应温度和时间对样品的晶型晶貌进行定向调控。结
论文部分内容阅读
以高锰酸钾为锰源,甘氨酸为模板在硝酸体系中仿生合成纳米二氧化锰。利用SEM、XRD、N2吸附脱附对制得样品进行表征,通过改变反应温度和时间对样品的晶型晶貌进行定向调控。结果表明,在反应时间1h,温度为70℃得到了片状花球-MnO2、90℃得到棒状-MnO2;而在70℃下反应8h则制得针花状-MnO2,通过实验分析得出纳米二氧化锰微观晶貌和晶型的演变规律。
Potassium permanganate as a source of manganese, glycine as a template in the nitric acid system biomimetic synthesis of nano-manganese dioxide. The prepared samples were characterized by SEM, XRD and N2 adsorption desorption. The crystal morphology of the samples was controlled by changing the reaction temperature and time. The results showed that the flake-MnO2 was obtained at 90 ℃ for 1h, the temperature was 70 ℃, and the rod-MnO2 was obtained at 70 ℃ for 8h, and the pin-flower-MnO2 was obtained by the experimental analysis The evolution of manganese dioxide microstructure and crystal form.
其他文献
目的 研究高血压伴阵发性心房颤动(PAf)患者触发性房性期前收缩(简称触发性房早)的电生理特点.方法 分析2008年4月至2011年3月经动态心电图确诊的46例高血压伴PMf患者(高血压
目的通过有限元数值计算的方法研究年龄变化对牙本质断裂力学行为的影响。方法根据典型的紧凑拉伸试件形式建立有限元模型,采用内聚力模型分别模拟裂纹在年轻和老龄牙本质中
目的 探讨围手术期应用鱼油对大鼠“术后疲劳”的影响.方法 60只SD大鼠,经术前1周行为学训练,以其结果为依据筛选出表现较差的12只为血清空白对照组,余48只按随机数字表法随
以七异丁基三硅醇POSS和三氯硅烷或三乙氧基硅烷化合物为原料,用“顶角-盖帽法”得到了一系列单官能POSS化合物。利用FT-IR、1 H-NMR、29SiNMR、DSC、XRD、TGA等对它们进行了
采用静电纺丝技术制备了不同质量比例的PLA/SF复合纳米纤维膜和不同载药量的PLA/SF复合纳米纤维膜。用傅里叶变换红外光谱和毛细流动孔隙测量仪研究复合纳米纤维膜的结构和孔
前臂黑色素痣位于暴露部位,不仅影响美观,且易与衣物等长期摩擦,存在恶变可能,需要及早治疗.面积较小者多采用非手术治疗,如液氮冷冻、激光汽化、化学腐蚀等,或行黑痣切除缝
基于导电填料(羧基功能化多壁碳纳米管,MWNTs-COOH)与聚氨酯间氢键相互作用基础上,制备了聚氨酯(PU)复合导电薄膜。表征结果证明,MWNTs-COOH和PU基体间存在着氢键相互作用,实
目的:探讨新生儿大肠埃希菌败血症的药物敏感特点,为合理治疗提供临床依据。方法:对成都市儿童医院新生儿科2007年1月～2010年12月收治的临床怀疑败血症的新生儿血标本进行培养
采用间歇法制备淀粉接枝丙烯酸的高吸水树脂,用红外光谱及XRD对共聚物结构进行了表征。在氧化淀粉的基础上探讨了引发剂用量、交联剂用量等反应条件的不同对吸水率、吸盐水率
比较静态交换与动态交换试验结果,发现在动态交换过程中,交换柱内纤维的利用率极低,吸附效率不到30%。通过模拟溶液在交换柱内扩散、吸附过程,得出由于交换柱内的纤维填充不