【摘 要】
：
In this paper, scrap rubber powder (SRP), azodicarbonamide (ADC) as foaming agent and double-component epoxy resins (ER) as binder were used to prepare porous sound-absorbing material of rubber foam composite (RFC) by hot-pressing process. Response surfac
【机 构】
：
School of Environment, Beijing Normal University, Beijing 100875, China;China Environmental Resource
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
In this paper, scrap rubber powder (SRP), azodicarbonamide (ADC) as foaming agent and double-component epoxy resins (ER) as binder were used to prepare porous sound-absorbing material of rubber foam composite (RFC) by hot-pressing process. Response surface methodology (RSM) was employed to evaluate three process variables, i e, specimen thickness (A), ADC dosage (B) and foaming temperature (C), and to establish two polynomial function model equation between sound absorption coefficient (α) and three process factors (A, B, C) at middle and low frequency 250 Hz, 500 Hz, 800 Hz, 1000 Hz to determine the optimal preparation condition of RFC. The statistical analysis of results demonstrated that specimen thickness (A) exerted significant impact on sound absorption properties of RFC. And the optimum prepared condition of RFC was 10 mm specimen thickness, 3.00 g ADC dosage, and approximately 196 ℃ foaming temperature. Under optimal condition, sound absorption coefficient of RFC could reach 5.68％ (250 Hz), 7.67％ (500 Hz), 20.73％(800 Hz), 18.71％ (1000 Hz), coinciding with the predicted values 5.70％ (250 Hz), 7.69％ (500 Hz), 20.77％(800 Hz), 18.74％ (1000 Hz) from the predicted polynomial function model, which exhibited that RSM could be used to optimize the preparation process of sound-absorbing materials.
其他文献
An adhesive of the SiBCN ceramic was synthesized through the polymer derived ceramics (PDC) route. Meanwhile with higher adhesion strength and simpler process condition, the polyborosilazane (PSNB) was modified by E-44 epoxy resin. The E-44 epoxy resin wa
We developed cordierite-mullite composite ceramic materials to package and encapsulate PCM, and presented a preparation process from raw materials of kaolin, talc and alumina. The properties and microstructre of cordierite-mullite composite ceramic were s
Structure and mechanical properties of Calcium silicate hydrate (C-S-H) at a molecular level act as “DNA” of cement-based construction materials. In order to understand loading resistance capability of C-S-H gel, research on molecular dynamics (MD) was ca
A mild chemistry route was developed to prepare carbonaceous nanofibers-titanium dioxide (CNF-TiO2) nanocomposites for removal of dye pollutants. In the process of the template-directed hydrothermal carbonization (HTC), ultrathin Te nanowires were adopted
The corrosion behavior and the effects of temperature on critical chloride content (Ccrit) of steel fibers in RPC were analyzed by a pH meter, ion chromatography, mercury intrusion porosimetry (MIP), and electrochemical techniques. It was found that the s
In order to enhance the fracture toughness of mullite,three-dimensional braided carbon fiber reinforced mullite (C/mullite) composites were prepared using the Al2O3-SiO2 sol with a high solid content as raw material.Mullitization behavior of the sol was c
The sulfate ions immobilization behavior of calcined layered double hydroxides (CLDHs) in the hardened cement paste was investigated. The experimental results show that the sulfate ions in cement paste are immobilized by CLDHs to reconstruct the layered s
To study the effect of atmospheric pressure on the properties of fresh and hardened air-entrained concrete, three kinds of air entraining agents were used for preparing air-entrained concrete in the plateaus (Lhasa, 61 kPa) and the plains (Beijing, 101 kP
In order to improve the thermal storage capacity of expanded vermiculite (EV) based form-stable composite PCM (FS-PCM) via organic modification of EV, first, EV was modified with a sodium stearate (NaSt) as surface modifier, and organic EV (OEV) with hydr
The experimental study of Bauschinger effect in Mn18Cr18N austenitic stainless steel was presented by compression-tensile cyclic loading tests with the prestrains ranging from 0.005 to 0.1, which was illustrated utilizing stress-strain curves and analysed