Cu_2O/TiO_2/Pt three-layer films were deposited on glass substrates using magnetron sputtering method.The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction(XRD), scanning electron microscopy(SEM), ultravioletvisible spectroscopy(UV-Vis) and photoluminescence spectroscopy(PL). The photocatalytic activity of the samples was evaluated by the photocatalytic degradation of methyl orange(MO) aqueous solution under visible light irradiation. The results indicate that the Cu_2O/TiO_2/Pt composite films are made up of three layers which are Pt layer,anatase-TiO_2 layer and Cu_2O layer from bottom to top. The surface of the films is even and composed of regular-shaped spherical particles. The photocatalytic activity of the Cu_2O/TiO_2/Pt three-layer film is much higher than that of the Cu_2O/TiO_2 double-layer film. Such enhancement is ascribed to the presence of Pt layer, which further inhibits the photogenerated electron-hole recombination, prolongs the lifetime of the photogenerated carriers, increases the quantum efficiency and hence improves the photocatalytic activity of the film effectively.
Cu_2O / TiO_2 / Pt three-layer films were deposited on glass substrates using magnetron sputtering method. The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), ultraviolet visible spectroscopy (UV-Vis) and photoluminescence spectroscopy (PL). The photocatalytic activity of the samples was evaluated by the photocatalytic degradation of methyl orange (MO) aqueous solution under visible light irradiation. The results indicate that the Cu_2O / TiO_2 / Pt composite films are The up of three layers which are Pt layer, anatase-TiO 2 layer and Cu 2 O layer from bottom to top. The surface of the films is even and composed of regular-shaped spherical particles. The photocatalytic activity of the Cu 2 O / TiO 2 / Pt three- Such enhancement is ascribed to the presence of Pt layer, which further inhibits the photogenerated electron-hole recombinat ion, prolongs the lifetime of the photogenerated carriers, increases the quantum efficiency and hence improves the photocatalytic activity of the film effectively.