Four kinds of aluminum based moderate temperature filler metals used for vacuum brazing of 6061 aluminum alloy were pre-pared by rapid solidification-isothermal rolling. The effects of alloy elements content on the melting characteristics of filler metals
【机 构】
：
Beijing Non-Ferrus Metals and Rare Earth Research Institute, Beijing 100012, China;Beijing Engineeri
论文部分内容阅读
Four kinds of aluminum based moderate temperature filler metals used for vacuum brazing of 6061 aluminum alloy were pre-pared by rapid solidification-isothermal rolling. The effects of alloy elements content on the melting characteristics of filler metals was stud-ied by Differential Scanning Calorimetry (DSC). The microstructures of the filler metals and brazed joints were observed by scanning elec-tron microscopy (SEM) and energy dispersive spectrometer (EDS). The results show that with the increase of Cu content into the filler metals,the liquid phase temperature gradually is decreased. Microstructure characterzation of the brazed joints shows the eutectic structure of (α+β) and (α+θ) decrease gradually, θ-CuAl2(Ni) gradually increases and transforms from small fishbone shapes to block shapes. Peak shear strength of 83 MPa for the 6061 aluminum joint with Al-9.5Si-10Cu-2Ni-0.5Mg was achieved after brazing at 575℃ for 2 min.
其他文献
0 前言rn冶金行业是指与冶炼金属相关、提供矿石(包括开采、选矿、勘探外贸等)、金属材料加工等方面的行业,主要分为黑色冶金和有色冶金两大类,作为重要的工业原材料供应部门,冶金工业为国民经济提供了丰富的金属材料,是工业经济发展的物质基础.目前我国已是世界第一冶金产业大国,钢产量和常用的有色金属产量都接近全球产量的一半,随着我国经济持续发展和基础设施的大力建设,未来冶金行业会持续快速发展.
The slag-free self-shielded flux-cored wire was fabricated to apply for the narrow gap welding. The results showed that narrow gap welding shows lower welding spatter compared with hardfacing except under voltage of 30 V and current of 260 A. The depositi
Aluminium matrix composites with 70％ volume fractions of SiC particles, as the reinforcements, were brazed in the vacuum fur-nace using Al-Si-Ti-Cu-In alloy as filler metal. The microstructure and constituent of the joints were examined by means of SEM an
The corrosion performance of aluminum/steel contact and aluminum/steel FSW joint in 3.5 wt.％ NaCl solution were analyzed using potentiostatic tests. The post-corrosion microstructure of the welding joint was characterized by optical microscope (OM), scann
The effect of fiber laser on MIG arc was investigated with 8 mm 7075-T6 high strength aluminum alloy as base material. The arc shape, droplet transfer form and electrical signal in the process of MIG welding and laser-MIG hybrid welding were analyzed. The
Friction stir welding (FSW), as a growing welding technology, from its genesis in 1991, was attended by many researchers in in-terdisciplinary fields of science and engineering. The current paper presents a bibliometric analysis of the subject and can be
In this paper, the microstructure of narrow gap laser welded joint of 45 mm Ti6321 titanium alloy was characterized. The micro-structure characteristics of Laser self-fusion and laser-multi-pass-narrow-gapfilling layer were observed by metallographic micr
党的十九届六中全会召开以来,在中央和国家机关行业协会商会第一联合党委的领导和指示下,中国建筑金属结构协会党支部高度重视十九届六中全会精神学习的任务,通过“自学+集中学”相结合,多措并举地开展系列学习活动.
The finite element simulation software SYSWELD is used to numerically simulate the temperature field, residual stress field, and welding deformation of Q690D thick plate multi-layer and multi-pass welding under different welding heat input and groove angl
在京津冀和长三角区域跨省市联网ETC示范工程实施的后期,交通运输部就开始考虑ETC的推广问题,为此要求部公路科学研究院(以下简称“公路院”)评估国内ETC应用的社会和经济影响、调查ETC带动的高新技术产业的情况、分析存在的问题,并就下一步的工作提出建议.2009年末至2010年10月期间,公路院向交通运输部公路局提交了一系列报告,包括《全国高速公路不停车收费情况调查》《关于制定国家推进不停车收费系统政策的建议》《不停车收费产业对经济和社会的支持情况》《关于制定不停车收费系统推广和补贴政策的建议》等.