Development of processing maps for as-cast ZE41A magnesium alloy

• 作 者: S. ANBU SELVAN S. RAMANATHAN R . KARTHIKEYAN B. K. RAGHUNATH
• 机 构: Department of Manufacturing Engineering, Annamalai University,Department of Mechanical Engineering,
• 出 处: Transactions of Nonferrous Metals Society of China
• 发表日期: 2010年01期

The hot deformation behavior of as-cast ZE41A magnesium alloy was studied by employing both processing maps and microstructural observations. To obtain processing map, hot compression tests were performed over a range of strain rates (0.001-1.0 s-1) and temperatures (250-450 ℃). Power dissipation efficiency (η) and instability parameter [ξ (ε)] were evaluated and processing maps were developed for the strain of 0.5. The dynamic recrystallization (DRX) and instable zones were identified and validated through micrographs. The processing maps can be used to select optimum strain rates and temperatures for effective hot working of the material.

The hot deformation behavior of as-cast ZE41A magnesium alloy was studied by employing both processing maps and microstructural observations. -450 ° C). Power dissipation efficiency (η) and instability parameters [ξ (ε)] were evaluated and processed maps were developed for the strain of 0.5. The dynamic recrystallization (DRX) and instable zones were identified and validated through micrographs. processing maps can be used to select optimum strain rates and temperatures for effective hot working of the material.