通过双丝埋弧焊接工艺性能试验、焊接接头力学性能试验及组织结构分析等,对Q420GJ钢的焊接性能及相关组织结构进行了研究。结果表明:焊接接头综合力学性能优良,接头抗拉强度达到590MPa,焊缝-40℃冲击功平均值KV2达到119J;热影响区的韧脆转变温度在-30℃附近;焊接接头过热区组织为贝氏体,焊缝中含有较多的针状铁素体。
Through the double-wire submerged arc welding process performance test, the mechanical properties of welded joints test and organizational structure analysis, Q420GJ steel welding performance and related organizational structure were studied. The results show that the mechanical properties of welded joints are excellent, the tensile strength of joints is 590MPa, the average KV2 of impact energy at -40 ℃ is 119J, the ductile-brittle transition temperature of heat-affected zone is around -30 ℃, the overheated zone of welded joint is Bainite, weld contains more acicular ferrite.
其他文献
着嗣后九卿科道等陈奏事件毋得泄漏事谕旨rn嘉庆十六年六月十二日rn嘉庆十六年六月十二日内阁奉上谕:向来九卿科道等遇有条陈纠劾,俱系封章入奏,呈递时面交外奏事官,转交内奏
目的:探讨炎性因子在冠心病中的表达,观察通心络对粥样斑块干预作用.方法:选择急性冠状动脉综合征(ACS组)患者44例,稳定型心绞痛(SAP)患者20例,正常对照组24例,比较各组间ToL
目的:探索并应用5F射频消融导管在经皮肾动脉交感神经消融术(catheter-based renal sympathetic denervation,RDN)治疗顽固性高血压患者中的安全性和有效性.方法:本次研究共
目的:探讨急性心肌梗死(AMI)患者外周静脉血单个核细胞尼克酰胺腺嘌呤二核苷酸磷酸(NADPH)氧化酶与左室重构的关系.方法:选择2010-12-2011-08住院治疗的77例AMI患者(AMI组)及
合作学习是一种创新学习方式,在小学语文教学过程中,应用该方式进行教学能够促进学生的团结性和探究性,以下对该教学方式的具体应用进行分析,目的在于提高小学语文教学水平.
目的:观察伴发高血压病(HP)的冠心病(CHD)患者行冠状动脉介入术(PCI)治疗后脂质过氧化损伤指标的变化并分析其意义.方法:选择32例CHD患者(A组)及38例CHD伴发HP患者(B组)进行P
雷·阿伦Ray Allen理查德·汉密尔顿Richard Hamilton康涅狄格大学素来以盛产射手闻名,作为史上投中三分球最多的雷·阿伦无疑是其中最伟大的一员,他的三分球命中数达到了261
目的:观察银杏叶提取物对冠心病不稳定型心绞痛(UA)低、中危患者疗效及炎性相关因子的影响.方法:132例冠心病UA低、中危患者随机分为治疗组(89例)和对照组(43例),对照组采用
读者朋友您好!为了让您的心声与杂志遥遥相系,为了让我们的付出能得到您的喜爱。请抽取少量时间在读者调查表上提出您最中肯的意见与想法。让我们与您一起共同担起杂志的命运
万历援朝东征战争(1592-1598)时期,辽东和畿辅的天津、山东是朝鲜战场主要的后勤供应基地,尤其是山东粮食,总数达“几千万斛”的“东粮”输送,不仅对这场战争,也对后来朝鲜人