The influence of different surface coatings of NiTi shape memory alloys was examined using in vitro testing methods. Plates of superelastic nickel-titanium shape memory alloy (NiTi) were coated with calcium phosphates (hydroxyapatite) by high-temperature plasma-spraying or by dip-coating. The biocompatibility was tested in vitro by cultivation of isolated human granulocytes and whole blood cells. As substrates, pure NiTi, plasma-spray-coated NiTi and dip-coated NiTi were used. Isolated granulocytes showed an increased adhesion to both calcium phosphate-coated NiTi samples. Compared to non-coated NiTi or dip-coated NiTi, the number of dead granulocytes adherent to plasma-sprayed surfaces was significantly increased (p<0.01). Whether the differences in apoptosis of granulocytes on dip-coated vs plasma-sprayed coatings observed are due to differences in material surface morphologies has to be analyzed in further studies. Because of the cellular interactions with the coating layers, it is likely that the results obtained are not caused by the underlying NiTi but due to the coating itself.
The influence of different surface coatings of NiTi shape memory alloys was examined using in vitro testing methods. Plates of superelastic nickel-titanium shape memory alloys (NiTi) were coated with calcium phosphates (hydroxyapatite) by high-temperature plasma-spraying or by dip- coating. The biocompatibility was tested in vitro by cultivation of isolated human granulocytes and whole blood cells. As substrates, pure NiTi, plasma-spray-coated NiTi and dip-coated NiTi were used. Isolated granulocytes showed an increased adhesion to both calcium phosphate- Compared to non-coated NiTi or dip-coated NiTi, the number of dead granulocytes adherent to plasma-sprayed surfaces was significantly increased (p <0.01). Whether the differences in apoptosis of granulocytes on dip-coated vs plasma- sprayed coatings observed are due to differences in material surface morphologies has been analyzed in further studies. Because of the cellular interaction with the coating layers, it is likely that the results obtained are not caused by the underlying NiTi but due to the coating itself.