【摘 要】
：
利用脱合金的方法以低铝含量的Ti6Al4V合金为前驱体,以NaOH溶液为电解质,成功制备了纳米多孔泡沫钛合金。通过动电位极化和恒电位极化对该体系的脱合金行为进行表征。结果表
【机 构】
：
西北有色金属研究院金属多孔材料国家重点实验室,
论文部分内容阅读
利用脱合金的方法以低铝含量的Ti6Al4V合金为前驱体,以NaOH溶液为电解质,成功制备了纳米多孔泡沫钛合金。通过动电位极化和恒电位极化对该体系的脱合金行为进行表征。结果表明:该体系的临界电压值为0.6 V。在临界电压附近,电流密度很快衰减。电压恒定在2.1 V时,电流快速增加到峰值后保持恒定。这是由Al的快速持续溶解所致。
Using the method of removing alloying, a Ti6Al4V alloy with low aluminum content was used as precursor and NaOH solution as electrolyte was used to prepare nano-porous titanium foam. The alloying behavior of the system was characterized by potentiodynamic polarization and potentiostatic polarization. The results show that the critical voltage of this system is 0.6V. Near the critical voltage, the current density decays rapidly. With a constant voltage of 2.1 V, the current rapidly increases to a peak value and remains constant. This is caused by the rapid and sustained dissolution of Al.
其他文献
目的：探讨五加生化胶囊用于药物流产后出血患者临床疗效。方法980例药物流产术后出血超过7 d的患者随机分为对照组490例，治疗组490例，对照组为药物流产出血后给予常规缩宫药物和
飞利浦2011“我行动·我绿动”百万节能承诺大行动于2011年11月23日在上海落幕。此次活动自今年3月启动以来，先后在全国近40个城市举办了推广活动，共收集到全国民众的节能承诺
血管支架的支撑性能及回弹性能是支架在结构设计过程中需要考虑的重要指标。本文选取M型支架节,通过有限元软件模拟,探究M型支架节的高度变化及结构设计波高比(h/H)对支架支
可拓学与TRIZ理论都是以矛盾问题为研究对象,对于如何处理矛盾问题都给出了比较成熟的理论及方法体系。这两种理论都是将哲学思想与数学、工程学相结合,最终用计算机技术来实
Li-S and Li-Se batteries have attracted tremendous attention during the past several decades,as the energy density of Li-S and Li-Se batteries is high (several
采用化学还原法,将六偏磷酸钠作为分散剂、硼氢化钠作为还原剂还原硝酸银,通过对比六偏磷酸钠不同含量及硼氢化钠与硝酸银的不同摩尔比寻找最佳条件制备出了纯无机体系下高度
通过模拟镦锻压缩和模锻实验研究Ti14合金半固态下的触变锻造特性,分析了锻造过程中的组织演变过程,测定了锻件的力学性能,并综合讨论了该合金半固态下的触变可锻性.结果表明
Herein,a facile strategy for the synthesis of sandwich pyrolyzed bacterial cellulose (PBC)/graphene oxide (GO) composite was reported simply by utilizing the la
A dual functional CNTs@graphene/CNTs cathode for Li–Se battery was constructed by a CNTs@graphene network and a CNTs interlayer. CNTs were first integrated wit
2011年11月10日，西门子参加2011中国国际绿色创新技术产品展。西门子展示了如何帮助中国城市大幅减少能源消耗和二氧化碳减排。除了能源、全面和绿色交通、照明和楼宇、工业生