论文部分内容阅读
The thickness of CoP thin films prepared by wet chemical deposition is of crucial importance on magnetic property and recording perform-ance. The coercivity of CoP films decreased with increasing film thickness. The coercivity was 45.37 kA m 1 at the thickness of 300 nm, and decreased to 21.65 kA m 1 at 5.7 μm. Recording performance tests indicate that, for drums with the same size, different recorded magnetic pole density have different thickness requirements. For 40 mm diameter magnetic drum, the optimal CoP thickness is 3～10 μm for 256 re-corded magnetic poles, 1～2 μm for 512 recorded magnetic poles, and 500～800 nm for 1024 recorded magnetic poles.
The thickness of CoP thin films prepared by wet chemical deposition is of crucial importance on magnetic property and recording perform-ance. The coercivity of CoP films decreased with increasing film thickness. The coercivity was 45.37 kA m 1 at the thickness of 300 nm, and decreased to 21.65 kA m 1 at 5.7 μm. Recording performance tests indicate that for drums with the same size, different recorded magnetic pole density have different thickness requirements. For 40 mm diameter magnetic drum, the optimal CoP thickness is 3 to 10 μm for 256 re-corded magnetic poles, 1 ~ 2 μm for 512 recorded magnetic poles, and 500 ~ 800 nm for 1024 recorded magnetic poles.