We sought to evaluate immediate and delayed micro-tensile bond strength of Panavia F2.0 and Multilink Sprint resin cement to superficial, deep and cervical dentin. Thirty-six freshly extracted non-carious human molars were sectioned in the mesiodistal direction to expose three different dentin regions including superficial dentin (1 mm below the dentine-enamel junction), deep dentin (1 mm above the highest pulp horn) and cervical dentin (0.5 mm above the cemento-enamel junction and 0.5 mm below the dentine-enamel junction). Resin cements were applied on dentin surfaces and composite blocks were luted under constant seating pressure. Each group was divided into three subgroups according to time intervals. Specimens were sectioned to obtain sticks of 1 mm 2 in diameter and subjected to microtensile bond strength testing at a cross head speed of 1 mm/min. Both resin cements showed higher micro-tensile bond strength to superficial dentin than that to deep or cervical dentin (P < 0.001). Micro-tensile bond strengths of Panavia F2.0 were higher than those of Multilink Sprint at different dentin regions (P < 0.001). Immediate micro-tensile bond strengths were higher than those of delayed micro-tensile bond strengths for both resin cements (P < 0.001). It was concluded that resin cements with different chemical formulations and applica-tions yield significantly different micro-tensile bond strengths to different dentin regions.
We sought to evaluate immediate and delayed micro-tensile bond strength of Panavia F2.0 and Multilink Sprint resin cement to superficial, deep and cervical dentin. Thirty-six freshly extracted non-carious human molars were sectioned in the mesiodistal direction to expose three different Dentin regions including superficial dentin (1 mm below the dentine-enamel junction), deep dentin (1 mm above the pulp fair) and cervical dentin (0.5 mm above the cemento-enamel junction and 0.5 mm below the dentine-enamel junction). Resin groups were divided on three subgroups according to time constant intervals. Each group was divided into three subgroups according to constant seating pressure. Each group was divided into three subgroups according to time seating intervals. Cross head speed of 1 mm / min. Both resin cements showed higher micro-tensile bond strength to superficial dentin than that to deep or cervical dentin (P <0.001). Mi cro-tensile bond strengths of Panavia F2.0 were higher than those of Multilink Sprint at different dentin regions (P <0.001). Immediate micro-tensile bond strengths were higher than those of delayed micro-tensile bond strengths for both resin cements (P <0.001). It was concluded that resin cements with different chemical formulations and applica- tions yield significantly different micro-tensile bond strengths to different dentin regions.