The hot deformation behavior of F6 NM stainless steel was investigated by hot compression test in a Gleeble-1500Dthermal-mechanical simulator.The flow strain-stress curves were obtained and the corresponding metallographic observation of this steel under different deformation conditions was also carried out.This steel exhibited dynamic recrystallization(DRX)in the temperature range of 1 273-1 473 Kand the strain rate range of 0.01-0.1s-1.The activation energy for hot deformation was determined to be 457.91kJ/mol,and the hot deformation equations were also established.The flow instability zone was determined and could be divided into two regions.The first one was located in the temperature range of 1 173-1 348 Kand the strain rate range of 0.056-10s-1,while the second one is in the temperature range of 1 398-1 448 Kand the strain rate range of 1.25-10s-1.In the end,the optimum conditions for hot working were provided.
The hot deformation behavior of F6 NM stainless steel was investigated by hot compression test in a Gleeble-1500 Dthermal-mechanical simulator. The flow strain-stress curves were obtained and the corresponding metallographic observation of this steel under different deformation conditions was also carried out.This steel exhibited dynamic recrystallization (DRX) in the temperature range of 1 273-1 473 Kand the strain rate range of 0.01-0.1 s-1. The activation energy for hot deformation was determined to be 457.91 kJ / mol, and the hot deformation equations were also established that the flow instability zone was determined and could be divided into two regions. first first was located in the temperature range of 1 173-1 348 Kand the strain rate range of 0.056-10s-1 while the second one is in the temperature range of 1 398-1 448 Kand the strain rate range of 1.25-10s-1. in the end, the optimum conditions for hot working were provided.