【摘 要】
：
In this research,2205/Q235B clad plates were prepared by a vacuum hot rolling composite process.The effects of adding Fe,Ni,and Nb interlayers on the bonding interface structures and the shear strengths of the clad steel plates were studied.The results sh
【机 构】
：
School of Materials Science and Engineering, Tianjin University, Tianjin 300350, China;Tianjin Key L
论文部分内容阅读
In this research,2205/Q235B clad plates were prepared by a vacuum hot rolling composite process.The effects of adding Fe,Ni,and Nb interlayers on the bonding interface structures and the shear strengths of the clad steel plates were studied.The results showed that 2205 duplex stainless steel and the three interlayers produced a large amount of plastic deformation and low-angle boundaries,and the main structures were the recrystallized and deformed grains.There were many recrystallized grains in the microstructure of the Q235B low-carbon steel due to the low deformation in the rolling process.The Fe interlayer had better wettability with the two kinds of steel,but the lower strength led to the reduction of shear strength by about 14 MPa compared with the original clad steel plate.The C element in the Q235B low-carbon steel easily diffused into the Fe interlayer,and the clad steel plate attained a poor corrosion resistance because a large decarburization area was formed.The Nb interlayer reacted with the Mo element in the 2205 duplex stainless steel to form an Nb-Mo binary alloy,which generated long-banded ferrite.The decarburization area was also produced because the Nb reacted with the C element in the Q235B to form hard and brittle NbCx.As a result,the shear strength was significantly reduced by about 282 MPa,and the corrosion resistance of the bonding surface was deteriorated.The Ni interlayer did not react with the alloy elements in both sides,and therefore effectively prevented element diffusion and improved the corrosion resistance of the bonding surface.Due to the low strength of the Ni interlayer and the increased number of bonding surfaces of the clad steel plates,the shear strength was reduced to some extent (about 40 MPa),but it still met the engineering application standards.
其他文献
A new kind of Mg-2Zn-0.6Ca (wt％) alloy was fabricated by casting and hot extrusion as a high-ductility structural material.The extruded alloy exhibits a superior elongation of ～ 30％,yield strength of 130 MPa and ultimate tensile strength of 280 MPa along
In the electromagnetic induction-controlled automated steel teeming (EICAST) technology of ladle,the height and location of the blocking layer are critical factors to determine the structure size and installation location of induction coil.And,they are al
The corrosion behavior of CoCrFeNiMox alloys was investigated in aqueous environments,NaCl and H2SO4 solutions,respectively,to simulate typical neutral and acidic conditions.The cyclic polarization curves in NaC1 and the potentiodynamic curves in H2SO4 cl
In addition to the advantage of the lightweight of magnesium alloys,magnesium composites have moderate strength and elastic modulus.The proposed application of magnesium composites as diesel truck pistons makes it necessary to assess their wear performanc
Single-pass compression tests were performed to investigate the hot deformation behavior of low-carbon boron microalloyed steel containing three various vanadium contents at 900-1100 ℃ and strain rate of 0.01-10 s-1 using the MMS-300 thermal mechanical si
Hot deformation behavior of 0.3C-15Cr-1Mo-0.5N high nitrogen martensitic stainless steel (HNMSS) was investigated in the temperature range of 1173-1473 K and at strain rates of 0.001-10 s-1 using a Gleeble 3500 thermal-mechanical simulator.The true stress
In this paper,we report the fabrication of the photocatalysts composed of Cu2O nanobelts and nanoporous Cu (NP Cu) substrate,which is obtained by soaking the NP Cu in dehydrated ethanol.The NP Cu substrate is achieved by dealloying of Ti40.6Zr9.4Cu40.6Ni6
Three-dimensional distribution of solute elements in an Mg-Zn--Gd alloy during ageing process is quantitatively characterized by three-dimensional atom probe (3DAP) tomography.Based on the radius distribution function,it is found that Zn-Gd solute pairs i
To explore the optimum use of stabilised elements and study the influences of stabilisation in 18Cr-2Mo grades,the Nb and Nb + Ti microalloying investigation focused on the relationships of the microstructure and mechanical properties of the microalloyed
Rutile (TiO2) particle-reinforced aluminum matrix composites were prepared by friction stir processing.The microstructure was studied using conventional and advanced characterization techniques.TiO2 particles were found to be dispersed uniformly in the co