Iron aluminides exhibit good resistance to high-temperature sulfidizing and oxidizing environments and potential for structural applications at high temperatures under corrosive environments. In this study, Fe-Al intermetallic compound was prepared by multi-layered roll-bonding of elemental Fe and Al foils. The process consisted of the accumulative roll-bonding (ARE) for making a laminated Fe/Al sheet and the subsequent heat treatment promoting a solid phase reaction in the laminated Fe/Al sheet. The microstructures produced at each processing stage were characterized by optical microscopy and scanning electron microscopy (SEM) equipped with energy dispersive X-ray spectroscopy (EDS). Vickers microhardness testing was used for hardness determination. A homogeneous intermetallic compound of Fe3Al or FeAl could be obtained after the subsequent heat treatment for 1.8 ks at 973 K and for 10.8 ks at 1123 or 1173 K.
Iron aluminumides exhibit good resistance to high-temperature sulfidizing and oxidizing environments and potential for structural applications at high temperatures under corrosive environments. In this study, Fe-Al intermetallic compound was prepared by multi-layered roll-bonding of elemental Fe and Al foils. The process consisted of the accumulative roll-bonding (ARE) for making a laminated Fe / Al sheet and the subsequent heat treatment promoting a solid phase reaction in the laminated Fe / Al sheet. The microstructures produced at each processing stage were characterized by optical microscopy Vickers microhardness testing was used for hardness determination. A homogeneous intermetallic compound of Fe3Al or FeAl could be obtained after the subsequent heat treatment for 1.8 ks at 973 K and for 10.8 ks at 1123 or 1173 K.