In this study,powder mixtures containing (Ti,W)C additions (10,20,30 and 40 wt％) were prepared and then consolidated at 1200,1250,1300 and 1350 ℃ by spark plasma sintering.The effect of (Ti,W)C additions on the microstructure and mechanical properties of
【机 构】
：
School of Mechanical Engineering, Nanjing University of Science and Technology, Nanjing 210094, Chin
论文部分内容阅读
In this study,powder mixtures containing (Ti,W)C additions (10,20,30 and 40 wt％) were prepared and then consolidated at 1200,1250,1300 and 1350 ℃ by spark plasma sintering.The effect of (Ti,W)C additions on the microstructure and mechanical properties of ultrafine WC-Co materials was investigated.The results demonstrate that the (Ti,W)C not only retards the sintering densification but also increases the porosity of sintered samples.The increasing sintering temperature is beneficial to the densification but results in the grain coarsening and the dissolution of W in (Ti,W)C.Moreover,there are no (Ti,W)C grains with obvious core/rim structure in the microstructure.With the (Ti,W)C increasing from 10 to 20 wt％,the hardness increases and fracture toughness changes hardly.However,the hardness and fracture toughness decrease slightly as the (Ti,W)C further increases.The transgranular fracture of (Ti,W)C phases is responsible for the slight reduction in fracture toughness.The sample with 20 wt％ (Ti,W)C has high hardness and fracture toughness (Hv: 21.3 GPa,KIc: 9.8 MPa m1/2).
其他文献
The effect of grain size on the mechanical properties of a high-manganese (Mn) austenitic steel was investigated via electron-backscattered diffraction,transmission electron microscope,X-ray diffraction,and tensile and impact tests at 25 ℃ and-196 ℃.The H
Sandwich-like Al/Ti/Al-laminated composites have many advantages such as low density and high specific strength with value in mechanical manufacturing and aerospace engineering.Here,Al/Ti/Al-laminated composites were fabricated by hot roll bonding and sub
Inadequate strength at the bone/cement interface is one of the main drawbacks of poly(methylmethacrylate) (PMMA) bone cement in the current orthopedic surgeries.In the present work,a partially degradable PMMA/Mg composite bone cement (PMC) was developed f
The microstructure,electrical conductivity and electromagnetic interference shielding effectiveness of Mg-X (X=Al,Sn,Y and Gd) alloys in as-cast and solution states were systematically investigated in this study.The electrical conductivity and electromagn
The thermal stability and mechanical properties of China low activation martensitic steel with Zr and Y were investigated via thermal aging at 550 ℃ for 8000 h.The Laves phase content monotonically increased with thermal aging,and the volume fraction of t
The hot deformation behavior and workability of a new reduced activation ferritic/martensitic steel named SIMP steel for accelerator-driven system were studied.The flow curve and its microstructure were studied at 900-1200 ℃ and strain rate range of 0.001
Carbon nanofiber (CNF)-reinforced aluminum-matrix composites were fabricated via ball milling and spark plasma sintering (SPS),SPS followed by hot extrusion and powder extrusion.Two mixing conditions of CNF and aluminum powder were adopted:milling at 90 r
The corrosion behavior of stainless steel exposed to a simulated salt lake atmosphere has been investigated by analyzing the evolution of surface morphologies and corrosion products,the initiation and development of pits,and the electrochemical characteri
In this study,the effect of cooling rates on microstructures and mechanical properties in a Al-bearing hot-rolled transformation-induced plasticity steel was investigated.The experiments were carried out using hot simulation machine and hot rolling mill,w
The influence of processing temperature on grain size reduction in AA 6063 aluminum alloy subjected to repetitive corrugation and straightening (RCS) is investigated in this work.The aluminum alloy was processed by RCS at different temperatures (room temp