摘要：在平时的生活中，我们总会看见有些建筑出现裂缝现象，有些裂缝非常大，有些比较小，无论裂缝大还是小，总会给我们带来心理上的恐惧感。其实，这些现象属于混泥土在施工过程中，由于受温度、气候，以及组成材料配备不合格等诸多因素构成。在众多的工程质量问题中，混凝土在施工过程中由于多方面原因出现一些裂缝，从而影响工程施工的质量，因此，必须十分重视混凝土裂缝成因的分析及预防。本文针对水泥混凝土施工中普遍存在的裂缝现象，进一步梳理裂缝产生的成因及防治技术。
关键词：混泥土施工裂缝成因防治
Abstract: in the usual life, we always see some buildings cracking phenomenon, some crack is very big, some are small, no matter big or small cracks, always bring us psychological fear. Actually, these phenomenon belongs to mixes clay in construction process, because by temperature, climate, and composition material equipped with unqualified, and many other factors. In many of the engineering quality problem, the concrete in the construction process due to various reasons some cracks, which affects the quality of the project construction, therefore, must be attached great importance to the concrete crack the analysis of the causes and prevention. This article in view of the cement concrete construction are common in the cracks of the phenomenon, further comb cracks the causes and prevention and control technology.
Keywords: mixes clay causes construction cracks in prevention and treatment
中图分类号： TV543+.6文献标识码：A 文章编号：
作为建筑工程的重要材料，混泥土的使用可谓是必不可少，特别是钢筋混泥土和水泥混泥土，重要性不言而喻。为了保证工程质量，以及保证施工顺利进行等多方面工作，把握好混泥土的质量关是关键之关键。本文所论述的混泥土是指通常讲的工程混泥土材料，即水泥作胶凝材料，砂、石作集料；与水（加或不加外加剂和掺合料）按一定比例配合，经搅拌、成型、养护而得的水泥混凝土。干密度为2000-2500kg/m3的水泥混凝土称为普通混凝土。随着国家城市化和工业化进程的推进，建筑工程如雨后春笋般突起，而这些建筑工程必须要使用混泥土材料。因此，搞好混泥土的配备以及调节构成比例等就显得非常重要，也是我们必须重视和值得研究的课题。
一、混泥土构成及混泥土裂缝种类
1、砖混结构与混凝土梁柱承重的区分
作为一种复合材料，混泥土专业的有：砖墙承重，叫做砖混结构，常用于层楼少的普通多层住宅，低价快捷；另一种叫混凝土梁柱承重，也叫框架结构，常用于十层以下的多层公共建筑；还有一种叫混凝土梁和混凝土墙承重，也叫剪力墙结构，经常用在一般的高层电梯楼，它们的区别是具备不同的水泥土限抗压强度。水泥土的无侧限抗压强度一般为0.5~4 Mpa，即比天然软土大几十倍至数百倍。图1．1是由水泥土无侧限抗压强度试验得到的应力-应变曲线。
水泥土应力一应变曲线
图中A5、Al0、A15、A20、A25分别表示水泥掺入比例=(5、10、15、20、25)％。
2、根据特征分类，可分为温差裂缝型、水泥干缩裂缝型等
通过特征不同，总体上我们可以分为：温差裂缝型、水泥干缩裂缝型、材料配备失衡裂缝、负荷型裂缝和施工操作不当等因素引起的裂缝。混凝土结构、构件出现裂缝，不但影响外观，而且有可能影响构件刚度和结构整体性。当裂缝程度不同，补救方法也不一样：如裂缝宽度>0.1mm的裂缝：板的裂缝处采取粘帖碳纤维布一层（200mg）加固方式，宽度以裂缝为中心向两侧延伸各200mm，长度为裂缝长度+400 mm(裂缝两端各延伸200mm)，两端各压100mm宽压条。又如整板出现结构性裂缝，或整板出现多条裂缝，或整板出现大面积开裂，采取双向碳纤维加固方式：东西方向100mm碳纤维布通长、间距100mm；南北方向100mm碳纤维布通长、间距100mm。因此，要根据裂缝的具体程度进行区别对待。
二、构成混泥土裂缝现象的成因
1、对有些结构按其所处条件的不同产生的混泥土裂缝
建筑裂缝的产生，总是给人以质量不过关、偷工减料、不专业等施工中不良印象。特别是对于一些非专业业主來说，这样的现象给人以危机之感。其实从专业的角度来说，在施工中对有些结构按其所处条件的不同，以及在安全可控范围内，是允许存在一定宽度裂缝的。尽管如此，但在作为负责任的施工单位和施工人员，在施工中一定要尽可能地采取有效技术措施，控制裂缝，使结构尽量不出现裂缝，或尽量减少裂缝的数量和宽度。
2、外部环境以及材料配备误差引起的混泥土裂缝
构成混泥土裂缝的成因繁多而且复杂，由于多种构成因素相互影响，还有外部环境以及材料配备误差等，也就是说，导致裂缝的产生有这样或那样的现象。由于裂缝的产生都有其产生的一种或几种原因，因此，要针对不同的裂缝，实行有效的补救。除上述因素以外，温度的变化以及含水量也能引起混泥土裂水泥土的含水量与被加固土体的含水量相比不超过5％，且随水泥掺入量的增加而逐渐降低。见表：
它们之间相互影响，把握不好就会引起裂缝。针对施工材料的质量问题以及施工材料配备等对混泥土产生裂缝的原因作全面的分析、总结，以便在出现问题时正确补救。
3、混泥土材料配备不合理引起的裂缝
混泥土材料配备不合理引起的裂缝，主要是由于混泥土构件的水泥、砂、骨料、拌和水及外加剂组成等配备不合理。首先，水泥一定要合符国家标准。骨料的选用最好用自然连续级配和碎石，碎石最大粒径应小于结构截面最小尺寸的1/4，且小于钢筋间距最小净距的3/4。同时又含有碱活性的骨料，一般选用中低强度的混凝土材料，其强度等级控制在C20～C35 范围为最合理，不要使用高强混凝土，容易开裂。
三、混泥土裂缝的防治方法
1、缜密的设计方案
设计对水泥混泥土裂缝的产生有着重要的影响。设计人员应该认真详细地根据施工的地理位置、地理环境、建筑的等级、地形状况、沿线地质和水文地质进行全面把握。设计要按照建筑的特点，按规范要求予以设计。同时，要根据当地实际情况，考虑建筑的承载量、以及气候因素等的影响，选择水稳性较好基层。此外，设计时还要设置完善的排水和必要的防护加固结构措施，尽可能考虑造成裂缝产生的诸多因素，设计一套科学缜密的设计方案，为保证施工质量做好前期准备。
2、精湛的施工技术
要想获得精湛的施工技术，必须要重视施工队伍的素质，选用有资质的施工单位和施工人员是工程质量的保证。混泥土裂缝产生的很大一部分原因，就是因为施工人员技术還不到位，没有按照标准严格要求自己，草率行事而产生。要坚决杜绝人为因素产生的水泥土开裂现象，造成不必要的损失。要把握好混泥土的质量关，首先要有专业的技术人员，高素质的施工队伍，同时还要有处理施工细节的耐心和责任心。比如在施工过程中，全面了解混泥土振捣时限以及有关要求，混凝土振捣密实后一定时间内，不得受到振动。拆除细节的把握，拆除时间要通过试验确定，一般可在混凝土强度达到2.5Mpa后拆除模板。养护处理，混凝土表面有模板覆盖时，应在养护期间经常使模板保持湿润。养护用水应与拌合水相同，每天洒水数次，以能保持混凝土表面经常处于湿润状态为度。混凝土达到2.5Mpa前，不得使其承受行人、运输工具、模板、支架等荷载，等等细节，都是要遵从和把握的关键。
3、值得注意的问题
施工时，要注意控制水泥与有机质的含量。混泥土中含沙量的多少直接影响混泥土结构抗拉强度以及收缩变形。砂石在进场之后要对其做压碎处理，并进行压碎值实验和筛分实验。混泥土配备，以及混泥土配置的参数比例一定要科学调配。针对水泥用量以及混泥土配料等材料进行科学配制，因为任何构成要件配备失误都会造成裂缝的产生。
重度：由于拌入软土中的水泥浆的重度与软土的重度相近，所以水泥土的重度与天然土的重度相近。表2.3为水泥土的重度试验结果。由表2.3可见，尽管水泥掺入比为25％，泥土的重度也仅比天然软土增加3％。因此采用深层搅拌加固厚层软土地基
导致混泥土开裂的另一个主要因素是用水量：本文中为了减少周围环境中空气湿度的变化对试验用土样含水量的影响，在使用土样之前，先用烘箱将天然土样进行烘干。通过公式中，把土样的含水量w统一定为12．28％，这样不仅可以使试验具有更高的精确性，同时也可以在后期强度分析时排除空气湿度和土样含水量的差异对水泥土强度影响。因此，本试验中水泥土试件制作所需的用水量由两部分组成，即按水灰比计算所得的用水量以及由土样含水量计算所得的用水量。用水量聊w的计算公式如下所示：
式中：mc-水泥的重量（g）；ms,d-被加固土样烘干后的重量（g）；W-土样含水量。
把握好用水量要严格按照标准来进行合理配备用水比列，确保混泥土质量。
参考资料：
[1]贾伟明．《混泥土梁板裂缝控制》，《科技风》2011年第13期
[2]杨丽玲 黄 威．《关于公路工程混泥土桥梁裂缝的探讨》，《中小企业管理与科技》2009年10月下旬刊
[3]胡永春．《现浇钢筋混泥土楼板裂缝分析》， 《中小企业管理与科技》 2010年5月
[4]李娟．《一些常见混泥土裂缝的成因及预防》，《科技与生活》2010年第11期
注：文章内所有公式及图表请以PDF形式查看。
关键词：混泥土施工裂缝成因防治
Abstract: in the usual life, we always see some buildings cracking phenomenon, some crack is very big, some are small, no matter big or small cracks, always bring us psychological fear. Actually, these phenomenon belongs to mixes clay in construction process, because by temperature, climate, and composition material equipped with unqualified, and many other factors. In many of the engineering quality problem, the concrete in the construction process due to various reasons some cracks, which affects the quality of the project construction, therefore, must be attached great importance to the concrete crack the analysis of the causes and prevention. This article in view of the cement concrete construction are common in the cracks of the phenomenon, further comb cracks the causes and prevention and control technology.
Keywords: mixes clay causes construction cracks in prevention and treatment
中图分类号： TV543+.6文献标识码：A 文章编号：
作为建筑工程的重要材料，混泥土的使用可谓是必不可少，特别是钢筋混泥土和水泥混泥土，重要性不言而喻。为了保证工程质量，以及保证施工顺利进行等多方面工作，把握好混泥土的质量关是关键之关键。本文所论述的混泥土是指通常讲的工程混泥土材料，即水泥作胶凝材料，砂、石作集料；与水（加或不加外加剂和掺合料）按一定比例配合，经搅拌、成型、养护而得的水泥混凝土。干密度为2000-2500kg/m3的水泥混凝土称为普通混凝土。随着国家城市化和工业化进程的推进，建筑工程如雨后春笋般突起，而这些建筑工程必须要使用混泥土材料。因此，搞好混泥土的配备以及调节构成比例等就显得非常重要，也是我们必须重视和值得研究的课题。
一、混泥土构成及混泥土裂缝种类
1、砖混结构与混凝土梁柱承重的区分
作为一种复合材料，混泥土专业的有：砖墙承重，叫做砖混结构，常用于层楼少的普通多层住宅，低价快捷；另一种叫混凝土梁柱承重，也叫框架结构，常用于十层以下的多层公共建筑；还有一种叫混凝土梁和混凝土墙承重，也叫剪力墙结构，经常用在一般的高层电梯楼，它们的区别是具备不同的水泥土限抗压强度。水泥土的无侧限抗压强度一般为0.5~4 Mpa，即比天然软土大几十倍至数百倍。图1．1是由水泥土无侧限抗压强度试验得到的应力-应变曲线。
水泥土应力一应变曲线
图中A5、Al0、A15、A20、A25分别表示水泥掺入比例=(5、10、15、20、25)％。
2、根据特征分类，可分为温差裂缝型、水泥干缩裂缝型等
通过特征不同，总体上我们可以分为：温差裂缝型、水泥干缩裂缝型、材料配备失衡裂缝、负荷型裂缝和施工操作不当等因素引起的裂缝。混凝土结构、构件出现裂缝，不但影响外观，而且有可能影响构件刚度和结构整体性。当裂缝程度不同，补救方法也不一样：如裂缝宽度>0.1mm的裂缝：板的裂缝处采取粘帖碳纤维布一层（200mg）加固方式，宽度以裂缝为中心向两侧延伸各200mm，长度为裂缝长度+400 mm(裂缝两端各延伸200mm)，两端各压100mm宽压条。又如整板出现结构性裂缝，或整板出现多条裂缝，或整板出现大面积开裂，采取双向碳纤维加固方式：东西方向100mm碳纤维布通长、间距100mm；南北方向100mm碳纤维布通长、间距100mm。因此，要根据裂缝的具体程度进行区别对待。
二、构成混泥土裂缝现象的成因
1、对有些结构按其所处条件的不同产生的混泥土裂缝
建筑裂缝的产生，总是给人以质量不过关、偷工减料、不专业等施工中不良印象。特别是对于一些非专业业主來说，这样的现象给人以危机之感。其实从专业的角度来说，在施工中对有些结构按其所处条件的不同，以及在安全可控范围内，是允许存在一定宽度裂缝的。尽管如此，但在作为负责任的施工单位和施工人员，在施工中一定要尽可能地采取有效技术措施，控制裂缝，使结构尽量不出现裂缝，或尽量减少裂缝的数量和宽度。
2、外部环境以及材料配备误差引起的混泥土裂缝
构成混泥土裂缝的成因繁多而且复杂，由于多种构成因素相互影响，还有外部环境以及材料配备误差等，也就是说，导致裂缝的产生有这样或那样的现象。由于裂缝的产生都有其产生的一种或几种原因，因此，要针对不同的裂缝，实行有效的补救。除上述因素以外，温度的变化以及含水量也能引起混泥土裂水泥土的含水量与被加固土体的含水量相比不超过5％，且随水泥掺入量的增加而逐渐降低。见表：
它们之间相互影响，把握不好就会引起裂缝。针对施工材料的质量问题以及施工材料配备等对混泥土产生裂缝的原因作全面的分析、总结，以便在出现问题时正确补救。
3、混泥土材料配备不合理引起的裂缝
混泥土材料配备不合理引起的裂缝，主要是由于混泥土构件的水泥、砂、骨料、拌和水及外加剂组成等配备不合理。首先，水泥一定要合符国家标准。骨料的选用最好用自然连续级配和碎石，碎石最大粒径应小于结构截面最小尺寸的1/4，且小于钢筋间距最小净距的3/4。同时又含有碱活性的骨料，一般选用中低强度的混凝土材料，其强度等级控制在C20～C35 范围为最合理，不要使用高强混凝土，容易开裂。
三、混泥土裂缝的防治方法
1、缜密的设计方案
设计对水泥混泥土裂缝的产生有着重要的影响。设计人员应该认真详细地根据施工的地理位置、地理环境、建筑的等级、地形状况、沿线地质和水文地质进行全面把握。设计要按照建筑的特点，按规范要求予以设计。同时，要根据当地实际情况，考虑建筑的承载量、以及气候因素等的影响，选择水稳性较好基层。此外，设计时还要设置完善的排水和必要的防护加固结构措施，尽可能考虑造成裂缝产生的诸多因素，设计一套科学缜密的设计方案，为保证施工质量做好前期准备。
2、精湛的施工技术
要想获得精湛的施工技术，必须要重视施工队伍的素质，选用有资质的施工单位和施工人员是工程质量的保证。混泥土裂缝产生的很大一部分原因，就是因为施工人员技术還不到位，没有按照标准严格要求自己，草率行事而产生。要坚决杜绝人为因素产生的水泥土开裂现象，造成不必要的损失。要把握好混泥土的质量关，首先要有专业的技术人员，高素质的施工队伍，同时还要有处理施工细节的耐心和责任心。比如在施工过程中，全面了解混泥土振捣时限以及有关要求，混凝土振捣密实后一定时间内，不得受到振动。拆除细节的把握，拆除时间要通过试验确定，一般可在混凝土强度达到2.5Mpa后拆除模板。养护处理，混凝土表面有模板覆盖时，应在养护期间经常使模板保持湿润。养护用水应与拌合水相同，每天洒水数次，以能保持混凝土表面经常处于湿润状态为度。混凝土达到2.5Mpa前，不得使其承受行人、运输工具、模板、支架等荷载，等等细节，都是要遵从和把握的关键。
3、值得注意的问题
施工时，要注意控制水泥与有机质的含量。混泥土中含沙量的多少直接影响混泥土结构抗拉强度以及收缩变形。砂石在进场之后要对其做压碎处理，并进行压碎值实验和筛分实验。混泥土配备，以及混泥土配置的参数比例一定要科学调配。针对水泥用量以及混泥土配料等材料进行科学配制，因为任何构成要件配备失误都会造成裂缝的产生。
重度：由于拌入软土中的水泥浆的重度与软土的重度相近，所以水泥土的重度与天然土的重度相近。表2.3为水泥土的重度试验结果。由表2.3可见，尽管水泥掺入比为25％，泥土的重度也仅比天然软土增加3％。因此采用深层搅拌加固厚层软土地基
导致混泥土开裂的另一个主要因素是用水量：本文中为了减少周围环境中空气湿度的变化对试验用土样含水量的影响，在使用土样之前，先用烘箱将天然土样进行烘干。通过公式中，把土样的含水量w统一定为12．28％，这样不仅可以使试验具有更高的精确性，同时也可以在后期强度分析时排除空气湿度和土样含水量的差异对水泥土强度影响。因此，本试验中水泥土试件制作所需的用水量由两部分组成，即按水灰比计算所得的用水量以及由土样含水量计算所得的用水量。用水量聊w的计算公式如下所示：
式中：mc-水泥的重量（g）；ms,d-被加固土样烘干后的重量（g）；W-土样含水量。
把握好用水量要严格按照标准来进行合理配备用水比列，确保混泥土质量。
参考资料：
[1]贾伟明．《混泥土梁板裂缝控制》，《科技风》2011年第13期
[2]杨丽玲 黄 威．《关于公路工程混泥土桥梁裂缝的探讨》，《中小企业管理与科技》2009年10月下旬刊
[3]胡永春．《现浇钢筋混泥土楼板裂缝分析》， 《中小企业管理与科技》 2010年5月
[4]李娟．《一些常见混泥土裂缝的成因及预防》，《科技与生活》2010年第11期
注：文章内所有公式及图表请以PDF形式查看。