【摘 要】
：
Al12Si3.75Ge0.25O26 ceramic powder was prepared by sol-gel method using Al(NO3)3,Si(OC2H5)4 and Cl3GeCH2-CH2COOH as precursors.The structural formation of Al12S
【机 构】
：
State Key Lab of Advanced Technology for Materials Synthesis and Processing
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
【基金项目】
：
教育部新世纪优秀人才支持计划;教育部留学回国人员科研启动基金
论文部分内容阅读
Al12Si3.75Ge0.25O26 ceramic powder was prepared by sol-gel method using Al(NO3)3,Si(OC2H5)4 and Cl3GeCH2-CH2COOH as precursors.The structural formation of Al12Si3.75Ge0.25O26 ceramic powder was analyzed by XRD.After reduction by flowing H2/Ar mixture gas,strong room temperature photoluminescence (PL) can be observed at 565 nm,613 nm,682 nm,731 nm and 777 nm,respectively.The PL intensity scarcely depends on the reduction temperature and duration,while the sample reduced at 500 ℃ for 3 hours has the highest PL intensity.Before and after reduction at 500 ℃,the volume of unit cell of mullite solid solution decreases to 0.4699 (A)3.Based on the analysis of XPS and Raman spectra,it can be approved that the PL phenomenon at room temperature is caused by the embedded Ge nanoparticles with the average size of about 1.95 nm.
其他文献
The microbial consortium used in continuous-flow,stirred tank processes to treat gold-bearing arsenopyrite concentrates became adapted to high concentrations of
NiO-Ce0.5Zr0.5O2catalysts were prepared by citrate method and used for hydrogen production from steam reforming of ethanol (SRE). The effect of nickel content a
A new biocatalyst route for the synthesis of a conducting polyaniline (PANI)/lignosulfonate (LGS) complex was presented.Four different catalysts such as hemoglo
Photopolymerization process of glycerin triglycidyl ether based systems was studied by an FT-IR spectrometer.An increase in the rate of polymerization for glyce
By a novel solid-state reaction process using amorphous C3N4 (a-C3N4) and transition metal oxides as starting reagents,cubic TaC,NbC and hexagonal WC nanopartic
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
The structure and properties of the glass-ceramics were tested with X-ray diffraction testing instrument,correlative software,and other modern testing means.The
Inhibition measurement of shrinkage of engineering cementitious composites(ECC) was investigated due to typical ECC with higher free drying shrinkage.The effect
The as-cast microstructure,mechanical properties and casting fluidity of ZA84 alloy containing TiC were investigated.The experimental results indicate that addi
A novel kind of denture base nanocomposite was prepared by polymethyl methyacrylate(PMMA) and cethyltrimethylammonium bromide modified organic montmorillonite (