,Modification effects of amphiphilic comb-like polysiloxane containing polyether side chains on the

• 作 者: Yanling QIAN Jianhua WANG Baoku ZHU Mei ZHANG Chunhui DU Youyi XU
• 机 构: Institute of Polymer Science,Zhejiang University,Key Laboratory of Macromolecular Synthesis and Func
• 出 处: 中国高等学校学术文摘·化学
• 发表日期: 2008年4期
• 关键词: poly(vinylidene fluoride) porous membrane comb-like polysiloxane containing poly

Amphiphilic comb-like polysiloxane (ACPS) containing polyether side chains was used as the modifica-tion reagent in the preparation of hydrophilic porous poly (vinylidene fluoride) (PVDF) membranes via a phase inversion process. The effects of ACPS on morphology, crystallinity, mechanical properties, reservation of ACPS in the phase inversion process, chemical structure, hydro-philicity and filterability performance of porous PVDF membranes were discussed. It was found that the addition of ACPS would result in the delayed demixing which yields "sponge-like" sublayers and longer crystallization time during the membrane formation process. It was revealed that O/F ratios of the bulk membrane were almost the same as those of the corresponding casting solutions which obviously indicated the high reservation of ACPS in the membrane formation process. The fact that the O/F ratios in the membrane surface layers were much higher than those in the bulk membrane proved the enrichment of ACPS on the surface. The filterability experiments and water contact angle testing proved the hydrophilicity of the blend membranes. Through a schem-atic model, the mechanism relating the membrane struc-ture and performance was interpreted. From the observed results, it can be concluded that ACPS acts as a potential candidate material for preparing PVDF membranes with extraordinary hydrophilicity and filterability.