日本东北大学与松下集团合作,采用新制成的高铁含量的纳米晶软磁合金(具有高磁感强度和低铁损),制成直径为70mm,高为50mm的定子,在相同转速和负载条件下,与厚为0.35mm的电工钢板制成的定子进行铁损比较。试验结果表明,所试制的纳米晶软磁合金NANOMET的铁损比电工钢降低了70%。东
Japan’s Tohoku University and Panasonic Group, the use of newly made high-iron content of nanocrystalline soft magnetic alloy (with high magnetic induction and low iron loss), made of diameter 70mm, height 50mm stator, at the same speed and load Under the conditions, and the thickness of 0.35mm made of electrical steel plate made of iron loss comparison. The experimental results show that the nano-soft magnetic nanomaterials NANOMET prepared by the iron loss is reduced by 70% compared with electrical steel. east