Effects of magnetic annealing on crystallization and magnetic properties of Nd_2Fe_(14)B/α-Fe nanoco

• 作 者: 王占勇 刘文庆 隋延力
• 机 构: School of Materials Science and Engineering,Shanghai Institute of Technology,Institute of Materials,
• 出 处: Journal of Rare Earths
• 发表日期: 2010年S1期
• 关键词: annealing coercivity annealed hysteresis magnetization accelerated heating ribbo

Crystallization and magnetic properties of Nd2Fe14B/α-Fe nanocomposite magnets have been investigated by annealing the as-spun ribbons with magnetic field.The crystallization process was accelerated by field annealing.The hysteresis loop became to be fat by magnetic annealing at 645 oC for 4 min,which was 690 oC for ribbons annealing without magnetic field.The relative content of α-Fe phase was increased from the results of XRD.The strength of the magnetic field had no obvious influence on the remanence and coercivity,but modified the squareness of hysteresis loop.

Crystallization and magnetic properties of Nd2Fe14B / α-Fe nanocomposite magnets have been investigated by annealing the as-spun ribbons with magnetic field. The crystallization process was accelerated by field annealing. The hysteresis loop became to be fat by magnetic annealing at 645 oC for 4 min, which was 690 oC for ribbons annealing without magnetic field. the relative content of α-Fe phase was increased from the results of XRD. strength of the magnetic field had no obvious influence on the remanence and coercivity, but modified the squareness of hysteresis loop.