【摘 要】
：
Zn(BTZ)2 was synthesized from the complex reaction between zinc acetate dihydrate and 2-(2- hydroxyphenyl) benzothiazolate. Then Zn(BTZ)2 was used as main light
【机 构】
：
Institute of Material Physics,Organic Solids Laboratory
【基金项目】
：
国家自然科学基金;天津市自然科学基金;天津市材料物理与化学基金;Tianjin Science Development Foundation for University;Tianjin Science Foundation
论文部分内容阅读
Zn(BTZ)2 was synthesized from the complex reaction between zinc acetate dihydrate and 2-(2- hydroxyphenyl) benzothiazolate. Then Zn(BTZ)2 was used as main light-emitting material doped with different amounts of fluorescent dye Rubrene and fabricated a series of white organic light emitting devices. The configurations were as follows: ITO/PVK:TPD/Zn(BTZ)2:Rubrene/Al. The doping concentration of Rubrene in Zn(BTZ)2 was 1.2%, 0.12%, 0.08% and 0.05%, respectively. According to the EL spectra and CIE coordinates of the above devices, the optimum doping concentration (0.05%, weight percent) had been determined. The steady and bright white light emitting of the device with 0.05% doping concentration had been obtained, and the white emission covered a wide range of driving voltage (10-22.5 V). The CIE coordinates were (x=0.341, y=0.334) at the driving voltage of 20 V, which was very close to the equi-energy point (x=0.333, y=0.333), and the corresponding luminance and external quantum efficiency were 4048 Cd/m2 and 0.63% (4.05 Cd/A), respectively. Lastly, we also discussed the emitting mechanisms of the material and the devices.
其他文献
In this paper, we prove the following estimateon exponential sums over primes: Let κ≥ 1, βκ = 1/2 + log κ/log 2, x ≥ 2 and α = a/q + λ subject to (a, q)
The Sinorhizobium meliloti C4-dicarboxylate transport (Dct) system is essential for symbiotic nitrogen fixation. The dctA gene, encoding the C4-dicarboxylate pe
通过求解N(N-)巴黎光学势的复薛定谔方程,研究了N(N-)系统的近阈束缚和共振行为,得到了一个p(p-)系统的 13P0共振态.发现其能量和宽度与最近BES用Breit-Wigner(B-W)公式分析J
The growing necessity of biomaterials has increased the interest in hydroxyapatite. Small differences in particle sizes, stoichiometry, morphology, crystallinit
Much attention has been paid to the natural mechanism of silkworm spinning due to the impressive mechanical properties of the natural fibers. In this work, we s
To investigate the vacuum-deposited films of the banana-shaped mesogens, we prepared a three-ring bent-core (that is, banana-shaped) compound m-bis(4-p- octoxys
“神龙一号”加速器是一台20MeV直线感应电子加速器.本文介绍了“神龙一号”的物理设计、研制过程和调试结果.物理设计中主要分析了加速器研制的技术难点,并给出各分系统应达
The growing process of a hydrogen blister in a wheel steel was observed in situ with an optical microscope, and the fracture surfaces formed from broken blister
The effects of preheating and pyrolysis temperatures and catalyst concentration on the synthesis of aligned carbon nanotubes (CNTs) using ferrocene as the catal
Single-wall carbon nanotubes (SWNTs) pre-decorated with functional molecules are directly aligned in the AC electric field, which makes SWNTs parallelly bridge