【摘 要】
：
本文运用电子探针扫描系统、俄歇能谱仪、透射电镜等,研究了Cr17Ni2钢高温回火脆性的产生原因。试验结果表明,这种钢在550℃左右回火时所产生的脆性属可逆回火脆性,并呈沿晶
论文部分内容阅读
本文运用电子探针扫描系统、俄歇能谱仪、透射电镜等,研究了Cr17Ni2钢高温回火脆性的产生原因。试验结果表明,这种钢在550℃左右回火时所产生的脆性属可逆回火脆性,并呈沿晶断裂。俄歇电子谱仪分析结果发现,回火脆的Cr17TNi2钢中,磷、铬、镍在奥氏体晶界上偏聚显著。透镜薄膜观察结果发现晶界和位错上有小质点析出。上述现象是高温回火脆性的产生原因。
In this paper, the electronic probe scanning system, Auger spectroscopy, transmission electron microscopy, Cr17Ni2 steel high temperature temper brittleness was studied. The test results show that the brittleness of this steel when it is tempered at about 550 ℃ is reversible temper brittleness and it is intergranular fracture. Auger electron spectroscopy analysis found that the temper brittle Cr17TNi2 steel, phosphorus, chromium, nickel in austenite grain boundary segregation significant. Lens film observation found that there are small grain boundaries and dislocations precipitation. The above phenomenon is the cause of high temperature temper brittleness.
其他文献
桑病毒病在广西蚕区桑园发生严重，发生率为40％左右，已成为广西桑的主要病害之一。尽管国内外对侵染桑的病毒种类有较多的描述，但是在公共数据库中来源于桑的病毒序列信息却非
金属黑色化处理常用于某些零件和产品的表面装饰,以及改善金属表面的性能,如抗蚀性、抗磨损性和抗辐射性等。黑色化处理方法很多,随金属材料和使用场合的不同,采用不同的配
本文提出了以偶氮氯膦Ⅰ为显色剂测定铍的吸光光度法。反应的合适酸度为pH4.8～5,络合物吸收峰位于600nm波长处,络合反应瞬间完成,至少稳定4小时。有混合掩蔽剂存在下,测得表观
葫芦科(Cucurbitacea)作物病毒病遍及世界各地,凡是种植瓜类作物的地区几乎都有病毒病的发生,常年发生率为1％～100％,各种瓜类作物都有过病毒病为害减产以至毁种的报道。目前,
为了更好地深入研究纳米磁珠吸附核酸的机理，研究核酸在具有不同修饰基团的纳米磁珠表面的吸附和脱附行为，首先我们制备了Fe3O4纳米微球以及4种不同基团修饰的纳米磁珠，以苯
类病毒(viroid)是一类单链共价闭合环状的RNA分子，由246～ 463个核苷酸组成，可侵染柑橘、苹果、葡萄、菊花及啤酒花等植物，引起植株矮化、叶脉变色、叶扭曲、叶局部褪绿或枯斑
番茄黄化曲叶病是由烟粉虱传双生病毒侵染引起的病毒病,是目前广东及华南地区番茄上主要病害。为了监测华南地区番茄黄化曲叶病的病原病毒种群动态,2009 ～ 2012年,分别从
分析健身操教学中学生产生心理障碍的原因,通过改变教学环境、教学方法,克服和消除学生练习时的心理障碍。
Analysis of aerobics teaching students to produce psychologi
Wheat plants with dwarf symptom were collected from Baoding and preserved in greenhouse.The virus was transmitted to maize by vector Laodelphax striatellus,
根据纳米磁珠非特异性吸附核酸的原理，我们研制开发同时提取多种类病毒或病毒核酸的高通量核酸提取方法，结合实时荧光RT-PCR技术，建立了多种植物类病毒的纳米磁珠实时荧光RT