【摘 要】
：
专用轧头外形如图1所示,它是采用CrWMn合金工具钢制造的。经淬火处理后,在使用过程中只轻轻一轧,尾部就断裂。实物断口晶粒粗细不一,图1中箭头1所指的尾部区域,断口呈粗大晶
论文部分内容阅读
专用轧头外形如图1所示,它是采用CrWMn合金工具钢制造的。经淬火处理后,在使用过程中只轻轻一轧,尾部就断裂。实物断口晶粒粗细不一,图1中箭头1所指的尾部区域,断口呈粗大晶粒,而逐渐向上,箭头2所指的区域则晶粒变细。在尾部外圆表面,有黑色网纹分布在箭头3所指的区域。对三个区域进行金相分析如下: 1.箭头1区域的基体组织如图2所示,主要为极粗大的白色针状淬火马氏体和多量残留奥氏体(暗
Special head shape shown in Figure 1, it is made of CrWMn alloy tool steel. After quenching, the use of only a slight rolling, the tail is broken. In-kind fracture varies in grain size. In the tail region indicated by arrow 1 in Fig. 1, the fracture is coarse and gradually upward while the region indicated by arrow 2 is finer. On the outer surface of the tail, there are black lines distributed in the area indicated by the arrow 3. Metallographic analysis of the three regions is as follows: 1. The matrix organization of the arrow 1 region is shown in Fig. 2, mainly consisting of extremely coarse white acicular quenched martensite and a large amount of retained austenite
其他文献
从将京津冀协同发展上升为重大国家战略,到京津冀一体化进入实质性推进阶段,再到全国第一个跨省市的区域“十三五”规划正式出炉……决心大、信心足、速度快、力度强,成为了
本文利用流动显示技术，观察并分析了内射流出口处的形状(大矩形、小矩形、正方形、大椭圆、小椭圆、圆形)改变时，以及射流出口处形成平面对称剪切流时，涡流的生成、发展、配对、
为了对水下细长体的流固耦合特性进行分析，本文建立细长体结构的平面运动学方程；为了捕捉结构的振动特性,采用双渐进法给出与之相应的体流动力学方程，形成以"流-刚-弹耦合"为特
具有微纳米结构的粗糙表面往往呈现出不同于光滑表面的疏水性质，这一疏水特性也逐渐被各行各业所应用。本文采用耗散粒子动力学(DPD)方法，分别研究了液滴在平坦壁面和有结
颗粒的碰撞演变是自然界存在的普遍的想象，它与人们的生活生产息息相关。通过PPT作者简单的介绍颗粒凝并的控制方程及处理该方程常用的数值方法。在这里最主要介绍一种矩
Super elliptical plates which are defined by shapes between an ellipse and a rectangle have a wide range of use in engineering applications, and the researc
会议指出,“十三五”期间,云南省“三农”工作成效显著.农业基础性地位持续巩固,粮食生产连年丰收,产量多年保持全国第十四位,全省生猪存栏连续稳居全国第四位.猪、牛、羊、
后卫在篮球队伍中占据着十分重要的位置,一名好的后卫能使球队在比赛中有良好的表现,甚至左右比赛的结果。通过分析华侨大学后卫古加尼得分、助攻等数据,明确学院篮球队后卫
研究了有限深两层流体中，斜入射的表面波和界面波与半无限自由弹性板的水弹性相互作用。在势流理论框架内，假设两层流体均是无粘的，不可压缩的且密度均为常数，运动是无旋的。
Temperature-dependent modulus of glass fiber/epoxy composite laminates were studied at temperatures ranging from room temperature up to 120℃.The storage mo