The functionally graded thermal barrier coatings (FG-TBCs) with 80 % ZrO2-13 % CeO2-7 % Y2 Os ( CYSZ)/NiCoCrAlY were prepared using a recently developed supersonic plasma spraying(S-PS) with dual powder feed ports system. The thermal shock experiment of FG-TBCs specimens was carried out by means of the automatic thermal cycle device, in which the samples were heated to 1 200 ℃ by oxygen-acetylene flame jet then waterquenched to ambient temperature. The temperature-time curves of specimens and photographs can be watched online and recorded by a computer during the test. The results show that the totally 1 mm-thick FG-TBCs have excellent thermal shock resistance due to the fact that the coatings have no any peeling-off after 200 thermal cycles. The microstructures and morphologies of FG-TBCs were characterized and analyzed by SEM.