【摘 要】
：
研究了不同玄武岩纤维掺量对C50防水混凝土抗压和抗折性能影响,并将试验结果与相同条件下聚丙烯纤维防水混凝土力学性能进行对比。试验研究表明:掺入玄武岩纤维和聚丙烯纤维
论文部分内容阅读
研究了不同玄武岩纤维掺量对C50防水混凝土抗压和抗折性能影响,并将试验结果与相同条件下聚丙烯纤维防水混凝土力学性能进行对比。试验研究表明:掺入玄武岩纤维和聚丙烯纤维后防水混凝土均表现出塑性破坏特征,试件抗压与抗折强度均有较大幅度提高。两种纤维对防水混凝土力学性能的影响规律基本一致。
The effect of different basalt fiber content on the compressive and flexural properties of C50 waterproofing concrete was studied. The test results were compared with the mechanical properties of polypropylene fiber waterproofing concrete under the same conditions. The experimental results show that the waterproof concrete with both basalt fibers and polypropylene fibers shows the characteristics of plastic failure, and the compressive strength and flexural strength of the specimens are greatly improved. The influence of the two kinds of fibers on the mechanical properties of waterproof concrete is basically the same.
其他文献
万达中心由坐落于四层裙楼上的南、北两栋高度和结构体系截然不同的两塔楼组成。南塔楼主体结构高度195.6m,北塔楼主体结构高度147.7m。工程结构存在大底盘、多塔楼、平面和
BEFORE going to the James Yen Institute, I met Qiu Jiansheng, one of the founders of the institute and currently director of the school office. He is a man of f
中国农业银行苏州分行大楼存在标准层平面为“L”形,扭转不规则；局部楼板不连续；局部竖向构件不连续等,属于特别复杂的高层建筑结构,给结构设计带来了一定的困难.结合抗震规范
昆山金鹰高层酒店结构总高度为220.8m,建筑地面以上49层,地面以下2层,结构采用框架-核心筒混合结构体系。在标高129.1m避难层处设置三道伸臂桁架及环带桁架,在标高192.1m避难
扬州东方国际大酒店位于江苏省扬州市江都区,地上65层,地下4层,建筑高度280.100m,为超限高层。塔楼采用混合框架-伸臂桁架-钢筋混凝土核心筒体系。介绍了结构设计重点和抗震
深圳腾讯滨海大厦两栋超高层塔楼由三道连体相连,裙房从塔楼主体悬挑而出,两栋塔楼高度不等,为非对称双塔连体结构.主体结构采用型钢混凝土框架-钢筋混凝土核心筒混合结构,连
大体积混凝土结构厚实,混凝土量比较大,通常采用地下现浇钢筋混凝土结构,所以工程条件比较复杂,对工艺技术有较高的要求,水泥水化热普遍超过25℃,结构物容易出现温度变形的情
通过对刚性桩复合地基桩侧阻力模型的假定,利用弹性力学的求解方法,推导不同侧阻力模型下刚性桩复合地的桩土应力比公式,并与现场试验数据对比,结果与实测数据吻合较好。由此
某高层结构地上36层,建筑总高度接近150m,主楼与纯地下室连成一体,置于同一个基础筏板上。主楼核心筒与其外围框架、主楼与纯地下室之间荷载差异大,地基基础须同时满足承载力
结合了无粘结技术施工简便和有粘结技术安全可靠特点的缓粘结预应力技术得到了较大的关注,并开始在实际工程中获得应用。考虑到预应力技术多应用于重要基础设施,其结构事故将