氢能通过多种方式进入金属材料结构件的内部,比如冶炼、加工、酸洗、电镀以及环境中服役过程.金属材料中的氢对材料力学性能、界面反应活性和环境促进开裂均有显著影响[1-7].曾一民[5]等曾研究了氢对镍钝化膜性能的影响.镍基合金或者铁镍基合金已应用于核电站关键部件.
氢对镍在弱碱性溶液中电化学行为的影响
【摘 要】
：
氢能通过多种方式进入金属材料结构件的内部,比如冶炼、加工、酸洗、电镀以及环境中服役过程.金属材料中的氢对材料力学性能、界面反应活性和环境促进开裂均有显著影响[1-7].曾一民[5]等曾研究了氢对镍钝化膜性能的影响.镍基合金或者铁镍基合金已应用于核电站关键部件.
【机 构】
：
上海大学材料研究所,上海,200072 中国核动力研究设计院反应堆燃料及材料重点实验室,成都,61
【出 处】
：
中国化学会第十七次全国电化学大会
【发表日期】
：
2013年2期
其他文献
Synthesis and electrochemical properties of graphene-modified LiCo1/3Ni1/3Mn1/3O2 cathodes for lithi
Previous investigations indicate that graphene can be used to effectively improve the electrochemical performance of LiFePO4 cathodes.LiCo1/3Ni1/3Mn1/3O2 (LCMNO) is a much more attractive cathode, and
Strong chemical interactions between the oxygen-containing functional groups on graphene oxide (GO) sheets and divalent metals ions were exploited for the softening of hard water.GO membranes were pre
Li4Ti5O12 with good crystallization and nanometer-size (18 nm) was in-situ grown on monolayer graphene (2 nm) using OmimCl as exfoliated agent.Such Li4Ti5O12/graphene nanostructure exhibits excellent
Reduced graphene oxide/ordered mesoporous carbon nanospheres composites used as supercapacitor elect
Graphene based carbon materials are promising electrodes for supercapacitors due to the high surface area, great conductivity of graphene, and remarkable chemical stability of the composites.In this p
P-phenylenediamine (PPD) functionalized graphene oxide (GO) materials (PPDG) were prepared through a one-step solvothermal process and their application as supercapacitors were studied.The structures
LiMnPO4/C materials were prepared by solid state reaction method by using traditional raw materials,surfactant-assisted precipitated NH4MnPO4·H2O as reactants respectively,and the structural and elect
会议
LiNi0.5Mn1.5O4是通过向LiMn2O4掺杂Ni得到的新一代高电压锂离子电池正极材料,其结构与LiMn2O4相似,为尖晶石结构.并当Ni代替部分Mn后,改善了Mn3+存在导致的LiMn2O4结构不稳定性,LiNi0.5Mn1.5O4具有高的能量密度、高的充放电平台、良好的倍率充放电性能以及低成本易于合成等优点,是正极材料中的研究热点.
会议
过渡金属氧化物作为Li-O2电池正极催化剂已有广泛的关注,其中Co3O4能够明显提高Li-O2电池的循环性能,引起了极大重视.我们在实验过程中发现,基于CoO制备的Li-O2正极催化剂与Co3O4正极催化剂相比,表现出更为突出的循环稳定性.
会议
合成了一种介孔碳材料,BET测试表明,比表面积为513.1143cm2/g,孔隙平均宽度为5.33311 nm,孔径主要分布在2-20nm之间.在此基础上,合成了介孔碳/硫复合材料,电化学研究表明,首次放电比容量为1419mAh/g,30次循环后放电比容量为369mAh/g.
氟化磷酸盐系列材料因氟离子的强电负性带来更高的电压,并且还可能出现两个或两个以上的电子转移,从而带来更高的比容量,因此近几年引起了人们的广泛关注.Na2MnPO4F,Li2MnPO4F有较合适的电压和较高的容量,加之Mn资源丰富等原因,是比较有发展潜力的新型钠/锂离子电池材料.
会议