【摘 要】
：
BA9913V medium-temperature curing epoxy resin for vacuum-bag molding process was prepared.Main physical and mechanical properties of BA9913V resin was teste
【机 构】
：
Resin and Prepreg Department of AVIC Composite Corporation Ltd.,Beijing 101300
【出 处】
：
第二届中国国际复合材料科技大会 (CCCM-2)
论文部分内容阅读
BA9913V medium-temperature curing epoxy resin for vacuum-bag molding process was prepared.Main physical and mechanical properties of BA9913V resin was tested and analyzed, and its cure kinetics was deeply investigated.The test results showed that BA9913V vacuum-bag molding resin could be cured at medium temperature environment, and showed good heat-resisting performances and mechanical performances.
其他文献
Polyarylacetylene is an attractive material due to its excellent high temperature resistant, susceptibility to oxidation at high temperature limits the rang
This paper introduces a flame retardant epoxy resin system.In 0.5h+90℃/90℃/1.5h ,its curing process under curing degree above 85%, oxygen index value is m
A series of low temperature curing polytriazole resins were designed and prepared from a variety of azides and alkynes through 1,3-dipolar cycloaddition rea
The curing reaction and curing kinetics were studied by differential scanning calorimetry(DSC).Curing reaction curves were tested with different heating-up
Except for its relatively high specific strength, specific stiffness and the ability to tailor their mechanical properties, the 1 to 2 order of damping abil
In order to improve the stiffness of epoxy matrix, polyfimctional epoxy resin was modified with amide acid oligomer, and the high modulus epoxy resin matrix
Rod-like silicate particles (attapulgite, ATT) were washed with deionized water and dried, ground and dried.Triethoxy(ethynyl) silane was used to modify ATT
Resin matrix composite is one of the basic materials for spacecrafts.High Performance Matrix Resins play an important role in improving the properties of co
High temperature resistant nitrile-based polymers, also named as phthalonitrile resins, are high performance thermosets obtained by the addition polymerizat
A novel heat-resistant polytriazole resin(C-PTA) and their carbon fiber-reinforced composites (C-PTA/T700) were prepared in this article.The storage propert